In this work a solution-annealed AISI 316H grade austenitic stainless steel was studied in terms of investigating the electrolytic hydrogen charging effects on the resulting Charpy impact toughness and dry sliding tribological behavior. Conventional Charpy impact bending tests were employed to study the mechanical response of the investigated material to dynamic loading conditions, whereas dry linear sliding tribological tests were used to study the material friction and wear behavior. The obtained mechanical and tribological properties were correlated with corresponding fracture and tribological mechanisms determined from morphological observations of fracture surfaces and tribological tracks. The applied testing procedures were individually carried out for the non-hydrogenated, hydrogen-charged, and dehydrogenated material conditions. The observed changes of individual properties due to applied hydrogen charging were rather small which indicated good resistance of the solution-annealed AISI 316H steel against material degradation in currently used electrolytic hydrogenation conditions.

Bubble (point defect) – a precursor of fuzz or under dense nanostructure formation is crystal lattice defect. Suitable selection of crystal lattice which inhibit Frenkel pair generation and intrinsically promotes self- interstitial solid solution strengthening contributes effectively towards making plasma facing material. For this, interstitial sites, their size, amount / fraction, positions, tendency of occupation and diffusion parameters (e.g. activation energies (Q), activation volumes) are determined. Fcc iron carbon alloys (austenitic stainless steels AISI / SAE 321, fcc structure, Pearson code cF4, space group Fm3̅m) are proposed as suitable candidates. Along with their room temperature fcc structure having 12 interstitial positions (4 octahedral, 6 coordination sites and 8 tetrahedral, 4 coordination sites / unit cell) to allow insertion of self (iron) atoms, they have excellent corrosion resistance, thermal conductivity, and non- magnetic properties. After their melting, casting, and machining to required dimensions and geometry, stabilizing heat treatment is applied to precipitate all carbon as TiC and prevent formation of Cr23C6 (sensitization). This resist heat and surface degradation and yield excellent architecture which not onlyinhibit Frankel pair generation but will also allow bulk assimilation or surface annihilation (loop punching) of this lattice point defect. A superior thermal, fluid, and structural design augment above. A second choice is presented as Co base superalloys owing to same fcc crystal structure and excellent properties (such as strength, dimensional stability, oxidation resistance) at high temperature.

The article presents a new method called slide roller burnishing (SRB) for cold working of cylindrical surfaces on machine tools, implemented with a novel multi-functional device. The machined material was chromium–nickel austenitic stainless steel. The deforming element is a toroidal roller whose axis crosses that of the workpiece. As a result, a relative sliding velocity occurs in the contact zone between the roller and the machined surface. The sliding velocity vector is set using the burnishing device. The theoretical background of SRB is presented. When the two axes are parallel, the well-known roller burnishing (RB) method is implemented. Thus, RB is a special case of SRB. Both processes are realized using the multi-functional burnishing device. The RB process was studied experimentally and optimized according to three criteria, based on the relationship between the surface integrity and operating behavio of the respective component, to achieve three processes: smoothing, hardening and mixed burnishing. Using the optimal RB parameters obtained, the dependence of the results of SRB on the crossing angle was investigated and optimized. A comparative analysis was performed between the optimized RB and SRB processes (respectively for their three variants: smoothing, hardening and mixed) based on geometrical and physical–mechanical characteristics of the surface integrity. The main advantage of the SRB is that it provides smaller height roughness parameters and a higher surface microhardness than RB.

The CMT (Cold Metal Transfer) arc welding process is a convenient instrument for the assembly of thin sheets [1], [2]. More particularly, it permits the decrease of the amount of heat transferred to the parts to-be assembled, thus reducing their subsequent deformations. The present work aims at simulating the CMT welding of thin stainless-steel sheets in order to develop an approach that allows the prediction of temperature fields, as well as final deformations induced by the welding process. For that purpose, instrumented tests and numerical simulations were set aiming at comparing the experiments with simulations. Butt-welding of stainless-steel sheets was considered, with a thickness ranging from 1 to 1.2 mm. The weld seam samples were observed in order to set an equivalent heat source for each configuration. Moreover, the electric current and voltage were surveyed, and temperature measurements were performed using K-type thermocouples. In addition, displacement measurements were obtained using the DIC (Digital Image Correlation) technique. Thermomechanical simulations were then carried out using an equivalent heat source approach, considering the phase changes of elements, i.e. the transitions from solid to liquid and from liquid to solid. These simulations also consider the actual geometry of seams induced by addition of a filler material.

Industries that rely on additive manufacturing of metallic elements, especially biomedical companies, require material science-based knowledge of how process parameters and methods affect element properties, but such phenomena are incompletely understood. In this study, we investigated the influence of selective laser melting (SLM) process parameters and additional heat treatment on mechanical properties. The research included structural analysis of residual stress, microstructure, and scleronomic hardness in low-depth measurements. Tensile tests with element deformation analysis using digital image correlation (DIC) were performed as well. Experiment results showed it was possible to observe the porosity growth mechanism and its influence on material strength. Elements manufactured with 20% lower energy density had almost half the elongation, which was directly connected with porosity growth during energy density reduction. Hot isostatic pressing (HIP) treatment allowed for a significant reduction of porosity and helped achieve properties similar to elements manufactured using different levels of energy density.

The main aim of this study is to investigate the optimization of the technological process for selective laser melting (SLM) additive manufacturing. The group of process parameters considered was selected from the first-stage parameters identified in preliminary research. Samples manufactured using three different sets of parameter values were subjected to static tensile and compression tests. The samples were also subjected to dynamic Split–Hopkinson tests. To verify the microstructural changes after the dynamic tests, microstructural analyses were conducted. Additionally, the element deformation during the tensile tests was analyzed using digital image correlation (DIC). To analyze the influence of the selected parameters and verify the layered structure of the manufactured elements, sclerometer scratch hardness tests were carried out on each sample. Basing on the research results it was possible to observe the porosity growth mechanism and its influence on the material strength (including static and dynamic tests). Parameters modifications that caused 20% lower energy density, elongation of the elements during tensile testing decreased twice, which was strictly connected with porosity growth. An increase of energy density by almost three times caused a significant reduction of force fluctuations differences between both tested surfaces (parallel and perpendicular to the building platform) during sclerometer hardness testing. That kind of phenomenon had been taken into account in the microstructure investigations before and after dynamic testing where it had been spotted a positive impact on material deformations based on fused material grains formation after SLM processing.

Chromium-nickel austenitic stainless steels are widely used due to their high corrosion resistance, good weldability and deformability. To some extent, their application is limited by their mechanical characteristics. As a result of their austenitic structure, increasing the static and dynamic strength of the components can be achieved by surface cold work. Due to the tendency of these steels to undergo intercrystalline corrosion, another approach to improve their mechanical characteristics is the use of low-temperature thermo-chemical diffusion processes. This article proposes a new combined process based on sequentially applied diamond burnishing (DB) and low-temperature gas nitriding (LTGN) to optimally improve the fatigue strength of 304 steel. The essence of the proposed approach is to combine the advantages of the two processes (DB and LTGN) to create a zone of residual compressive stresses in the surface and subsurface layers–the enormous surface residual stresses (axial and hoop) introduced by LTGN, with the significant depth of the compressive zone characteristic of static surface cold working processes. DB (both smoothing and single-pass hardening), in combination with LTGN, achieves a fatigue limit of 600 MPa, an improvement of 36.4% compared to untreated specimens. Individually, smoothing DB, single-pass DB and LTGN achieve 540 MPa, 580 MPa and 580 MPa, respectively. It was found that as the degree of plastic deformation of the surface layer introduced by DB increases, the content of the S-phase in the nitrogen-rich layer formed by LTGN decreases, with resultant increased content of -phase, and a new (also hard) phase: stabilized nitrogen-bearing martensite.

A multi-strand composite welding wire was applied to join high nitrogen austenitic stainless steel, and microstructures and mechanical properties were investigated. The electrical signals demonstrate that the welding process using a multi-strand composite welding wire is highly stable. The welded joints are composed of columnar austenite and dendritic ferrite and welded joints obtained under high heat input and cooling rate have a noticeable coarse-grained heat-affected zone and larger columnar austenite in weld seam. Compared with welded joints obtained under the high heat input and cooling rate, welded joints have the higher fractions of deformed grains, high angle grain boundaries, Schmid factor and the lower dislocation density under the low heat input and cooling rate, which indicate a lower tensile strength and higher yield strength. The rotated goss (G_RD) orientation of a thin plate and the cube (C) orientation of a thick plate are obvious after welding, but the S orientation at 65° sections of Euler’s space is weak. The δ-ferrite was studied based on the primary ferrite solidification mode. It is observed that low heat input and high cooing rate result in the increasing of δ-ferrite and high dislocation density was obtained in grain boundaries of δ-ferrite. M₂₃C₆ precipitates due to low cooling rate and heat input in weld seam and deteriorates the elongation of welded joints. The engineering stress-strain curves also show the low elongation and tensile strength of welded joints under low heat input and cooling rate, which is mainly caused by the high fraction of δ-ferrite and the precipitation of M₂₃C₆.