Titanium dioxide (TiO₂) micro and nano architectures have been intensively studied in the past years because of many varied applications in environmental, energy conversion, and storage fields, such as heterogeneous catalysis, dye-sensitized solar cells, lithium/sodium ion batteries, lithium-sulfur (Li-S) batteries, and bio-nanotechnology, etc. Especially the surface and interface structures in the TiO₂ structures play important roles in those applications. This mini review article focuses on TiO₂ micro and nano architectures with the prevalent crystal structures (anatase, rutile, brookite, and TiO₂(B)), and summarizes major advances in the surface and interface engineering and applications in environmental and electrochemical applications. We present the principles and growth mechanisms of TiO₂ nanostructures via different strategies, with an emphasis on rational control of the surface and interface structures. We further discuss the applications of TiO₂ micro and nano architectures in photocatalysis, lithium/sodium ion batteries, and Li-S batteries. Throughout the discussion, the relationship between the device performance and the surface structures of TiO₂ micro/nano structures will be highlighted. Then we discuss the phase transitions of TiO₂ nanostructures and possible strategies of improving the phase stability. The review concludes with a perspective on the current challenges and future research directions.

Increasing the loading density of nanoparticles on carbon support is essential for making Pt-alloy/C catalysts practical in H2-air fuel cells. The challenge lies in increasing the load-ing while suppressing the sintering of Pt-alloy nanoparticles. This work presents a 40% Pt-weighted sub-3 nm PtCo/C alloy catalysts via a simple incipient wetness impregnation method. By carefully optimizing the synthetic conditions such as Pt/Co ratios, calcination temperature and time, the size of supported PtCo alloy nanoparticles is successfully con-trolled below 3 nm, and a high electrochemical surface area achieves of 94 m2/g is achieved, which is 2.8 times of commercial PtCo/C-TKK catalysts. Demonstrated by elec-trochemical oxygen reduction reaction, PtCo/C alloy catalysts present an enhanced mass activity of 0.45 A/mg at 0.9 V vs. RHE, which is 1.7 times that of PtCo/C-TKK catalyst. Therefore, the developed PtCo/C alloy catalyst can potentially be a highly practical cata-lyst for H2-air fuel cells.