Chaphamaparvovirus (ChPV) is an ancient virus that has been detected in a variety of hosts. In this study, based on the phylogenetic analysis and the adaptability of ChPV to multiple hosts, we evaluated the potential of feline (FeChPV) and canine ChPV (CaChPV) for cross-species transmis-sion. Phylogenetic analysis showed that FeChPV and CaChPV were closely related. Notably, two strains of ChPVs isolated from domestic cats and 2 from dogs clustered together with CaChPVs and FeChPVs, respectively, suggesting the stringent boundaries between canine and feline ChPV may be broken. Further analysis revealed that CaChPV and FeChPV were more adapted to dogs than to cats, strongly suggesting the possibility of unidirectional or bidirectional transmission be-tween dogs and cats. Mutation analysis identified several shared mutations in cross-species-transmissible strains that were not located within immune epitopes. Furthermore, the VP struc-tures of FeChPV and CaChPV exhibited a high degree of similarity across both cross-species-transmissible and non-cross-species-transmissible strains. However, definitive experimental evi-dence is lacking, and its capacity for cross-species transmission should be approached with cau-tion and elucidated in further studies.

In this paper, the sol−gel method was used to synthesize powders of LaMnO3 (LMO), La0.85Ca0.15MnO3 (LCM), and La0.85Sr0.15MnO3 (LSM). We investigated the impact of substituting Ca and Sr at the A−site on the perovskite crystal structure and electrochemical capabilities of LMO. LCM retained its orthogonal structure in comparison to the parent LMO components, whereas LSM transitioned to a rhombic structure. At 0.5 A/g, the specific capacitance of LCM and LSM electrodes is 185.5 F/g and 248 F/g, respectively.The specific capacitance of LCM was more three times than that of the LMO electrode. Among the three samples (LMO, 22.25 m2 g−1; LSM, 31.56 m2 g−1), the LCM sample exhibited the highest specific surface area of 38.79 m2 g−1. The charge transfer resistances of the LMO, LCM, and LSM are 0.48 Ω, 0.36 Ω, and 0.38 Ω, correspondingly. The LCM electrode exhibits the greatest capacitance performance due to its more refined morphology, increased concentration of oxygen vacancy, and more complete utilization of the perovskite bulk structure. The above results demonstrate that Ca or Sr substitution of A−site compounds has great potential for supercapacitor applications.