A method for accurately determining the chemical composition of deposits at the bottom of pores during the electrocoloring (e-coloring) of aluminum anodic oxide (AAO) layers in tin-based solutions is developed. The aluminum samples were AC e-colored after DC sulfuric anodization. Free-standing, tin e-colored aluminum oxide film was obtained by selective dissolution of the metallic aluminum from the AAO in copper chloride solution to access the deposit directly at the bottom of the pore. This allowed us to take XPS analysis directly from the deposits at pore bottoms without any interference from the base material or insulating barrier layer. The results revealed the presence of a mixture of tin oxide and metal in the deposits, which were richer in oxide content. Furthermore, a cyclic voltammetry experiment mimicking real polarization conditions during AC conditions was optimized and used to gain a deeper understanding of the electrochemical reactions that occur during AC electrocoloring. The comparison of CV results in tin-free and tin-containing electrolytes indicated that the tin deposited during a cathodic cycle is oxidized in the anodic cycle. The formation of tin based deposits radically changed the CV behavior. The XPS and cyclic voltammetry results consistently show that the deposits formed during e-coloring comprised a mixture of metallic and oxidic tin species richer in oxide content.

A Cu₂ZnSnS₄ (CZTS) film with a thickness of approximately 1.5 μm was fabricated on a Mo-coated glass substrate by annealing a CZTS precursor fabricated from nanoparticle ink. The chemical states of the elements in the CZTS thin film in the depth direction were studied to identify the presence of secondary phases, which are detrimental to the performance of solar cells containing CZTS. X-ray diffraction was unable to detect any secondary phases in CZTS because of their small relative amount. Instead, X-ray photoelectron spectroscopy (XPS), which is highly sensitive to chemical state, was conducted at different depths in the CZTS film to further check the presence of secondary phases. XPS analysis revealed peaks shift consistent with the presence of secondary phases. For the CZTS film annealed in a S atmosphere at 575 °C for 3 h, the film surface consisted of a secondary-phase layer composed of CuS, ZnS, and SnSx (x=1 or 2) originating from the decomposition of CZTS. At depths below 80 nm, the film was pure CZTS. Formation of MoS2 at the CZTS–Mo interface was confirmed by XPS analysis of Mo and S.

The reduction of Ce cations in CeO2 can be enhanced by its partial substitution by Fe cations. The enhanced reduction of Ce cations results in a considerable increase in the reaction rates for thermal water splitting reaction when compared to CeO2 alone. This mixed oxide has a smaller crystallite size when compared to CeO2 in addition to a smaller lattice size. In this work, two Fe-substituted Ce oxides are studied (Ce0.95Fe0.05O2 and Ce0.75Fe0.25O2) by core and valence level spectroscopy in their as-prepared and Ar-ions sputtered states. Ar-ions sputtering substantially increases Ce4f lines at about 1.5 eV below the Fermi level. In addition, it is found that the XPS Ce5p/O2s ratio is sensitive to the degree of reduction, most likely due to a higher charge transfer from the oxygen to Ce ions upon reduction. Quantitatively it is also found that XPS Ce3d of the fraction of Ce3+ (uo, u’ and vo, v’) formed upon Ar-ions sputtering and the ratio Ce5p/O2s lines are higher for reduced Ce0.95Fe0.05O2 than for reduced Ce0.75Fe0.25O2. XPS Fe2p showed however no preferential increase for Fe3+ reduction to Fe0 with increasing time for both oxides. Since water splitting was higher on Ce0.95Fe0.05O2 when compared to Ce0.75Fe0.25O2, it is inferred that the reaction centers for the thermal water splitting to hydrogen are the reduced Ce cations and not the reduced Fe cations. These reduced Ce cations can be tracked by their XPS Ce5p/O2s ratio in addition to the common XPS Ce3d lines.

Low separation efficiency of photogenerated carriers and inefficient utilization of visible light limit the application of g-C3N4 nanosheets (CNNs) in the field of photocathodic protection (PCP). Therefore, this work considered indium zinc sulfide (ZnIn2S4, ZIS) as a visible photosensitizer and an electronic donor to promote its PCP performance. ZIS nanolayers with nano-leaf structures were fabricated on CNNs by a simple hydrothermal method. The synthesized 30% ZIS@CNNs composites significantly enhanced the PCP performance for 316 stainless steel (SS) compared with pure CNNs. Under visible light illumination, the 30% ZIS@CNNs photoelectrode exhibited the largest photoinduced current density of 17.30 μA cm−2 and a photoinduced potential drop of 0.37 V, which was approximately 4 and 7.5 times higher than that of pure CNNs, respectively. The improved protection performance may be attributed to the significant increase in visible light absorption and the great enhancement in the separation efficiency of

In this study we present gas-phase fluorination as a method to create a thin LiF layer on Li6.5La3Zr1.5Ta0.5O12 (LLZTO). We compare these fluorinated films with LiF films produced by RF-magnetron sputtering, where we investigated the interface between the LLZTO and the deposited LiF showing no formation of a reaction layer. Furthermore, we investigate the ability of this LiF layer as a protection layer against Li2CO3 formation in ambient air. By this we show that Li2CO3 formation is absent at the LLZTO surface after 24 h in ambient air supporting the protective character of the formed LiF films and hence could enhance the handling of LLZTO in air for battery production. With respect to the use within hybrid electrolytes consisting of LLZTO and a mixture of polyethylene oxide (PEO) and Lithium bis(trifluoromethanesulfonyl)imide (LiTFSI) we also investigated the interface between the formed LiF films and a mixture of PEO LiTFSI by X-ray photoelectron spectroscopy (XPS) showing decomposition of the LiTFSI at the interface.

The interest on amorphous carbon thin films with low secondary electron yield (SEY) has been increasing in the last years, to mitigate electron multipacting in particle accelerators and in RF devices. Previous works found that the SEY increases with the hydrogen amount and correlates with the Tauc gap. In this work, we analyse films produced by magnetron sputtering with different contents of hydrogen and deuterium, incorporated via target poisoning and sputtering of CxDy molecules. XPS was implemented to estimate the phase composition of the films. The maximal SEY was found to decrease linearly with the fraction of the graphitic phase in the films. These results are supported by Raman scattering and UPS. The graphitic phase decreases almost linearly for hydrogen and deuterium concentrations between 12% and 46% (at.), but abruptly decreases when the concentration reaches 53%. This vanishing of the graphitic phase is accompanied by a strong increase of SEY and of the Tauc gap. These results suggest that the SEY is not dictated directly by the concentration of H/D but by the fraction of graphitic phase. The results are supported by a model used to calculate SEY of films consisting of a mixture of graphitic and polymeric phases.

Super-hydrophobic surfaces and coatings have stimulated a great deal of research, with the aim to achieve better wetting properties. Factors such as surface chemistry and roughness play an important role in changing the surface energy, which in turn leads to changes in the wettability. Here, we have analysed the time dependence of the oxide layer and possible surface adsorbates on the surface topography of an Al59Cu25Fe13B3 quasicrystalline material for changes to the wettability. The quasicrystalline matrix phase was 94 % of the sample volume, and covered by a very smooth, amorphous oxide layer. The AlB12 and AlFe2B2 boron-rich phases were embedded in the quasicrystalline material as a result of a 3 at.% boron addition, which makes atomisation of the material a simpler process. Under ambient conditions the sample was naturally covered by an oxide layer; therefore, it is referred to as “surfenergy”, to distinguish it from the conventional surface energy of a bare quasicrystal surface. The growth of the oxide layer with atmospheric ageing and annealing at 500° C in air for various times was investigated for both cases. The phase most prone to oxidation was the boron-rich AlFe2B2, which influenced the topography of the surface and accordingly the wetting behaviour of the specimen. We demonstrated that the surfenergy depends on the polar component, which is the most sensitive to the operating conditions. A correlation between the surfenergy components and the surface roughness was found. In addition, theoretical models to determine the wettability were included.

Delayed atomic layer deposition (ALD) of ZnO, i.e., area selective (AS)-ALD, was successfully achieved on silicon wafers (Si/SiO2) terminated with tris(dimethylamino)methylsilane (TDMAMS). This resist molecule was deposited in a home-built, near atmospheric pressure, flow-through , gas-phase reactor. TDMAMS has been shown to react with Si/SiO2 in a single cycle/reaction and to drastically reduce the number of silanols that remain at the surface. ZnO was deposited in a commercial ALD system using dimethylzinc (DMZ) as the zinc precursor and H2O as the coreactant. Deposition of TDMAMS was confirmed by spectroscopic ellipsometry (SE), X-ray photoelectron spectroscopy (XPS), and wetting. ALD of ZnO, including its selectivity on TDMAMS – terminated Si/SiO2 (Si/SiO2/TDMAMS), was confirmed by in situ ellipsometry, ex situ SE, XPS, and/or high sensitivity – low energy ion scattering (HS-LEIS). The thermal stability of the TDMAMS resist layer, which is an important parameter for AS-ALD, was investigated by heating Si/SiO2/TDMAMS in air and nitrogen at 330 ºC. ALD of ZnO takes place more readily on Si/SiO2/TDMAMS heated in the air than in N2, suggesting greater damage to the surface heated in the air. To better understand the in situ ALD of ZnO, the data were also plotted as the normalized growth per cycle and to show the selectivity. Even one, short pulse of TDMAMS effectively passivates Si/SiO2. TDMAMS can be an effective small molecule inhibitor of ALD of ZnO on Si/SiO2 surfaces.

Mechanically strong and thermally stable films obtained from a water-based polyurethane (PU) dispersion with small (0.1–1.5 wt.%) additions of graphene oxide nanosheet (GO) were studied through elemental analysis, X-ray photoelectron spectroscopy, differential thermogravimetry, and Raman spectroscopy. Moreover, the depletion of near-surface layers in nitrogen was presented for all the samples under study. It was found that the introduction of GO into a PU matrix was ac-companied by a partial reduction of graphene oxide nanosheet and an increase in the concentra-tion of defects in its structure.

Graphene-oxide (G) was prepared by the Hummers’ method. A G-COOH layer was synthesised using chloroacetic acid and G. To fabricate carboxylated graphene-RuO2 (G-COORu) nano¬¬-composites, RuO2 nano particles were grown on graphene layers using a one-step thermal method, -COOH(G-COOH), and RuCl3. All materials were characterised using X-ray diffraction, transmission electron microscopy, scanning electron microscopy, 13C-nuclear magnetic resonance as well as X-ray photoelectron, Fourier-transform infrared spectroscopy, and Raman. The electrochemical characteristics of the G-COORu supercapacitors were analysed using electrochemical impedance spectroscopy, cyclic voltammetry, constant current charge–discharge tests, and Nyquist impedance plots. The supercapacitors exhibit a specific capacitance of ~125 F g-1 at 100 mA cm-2 within the potential range of 0–1.0 V. The method used here provides a simple approach for the deposition of RuO2 nano particles on graphene layers and can be widened to the fabrication of other classes of hybrids based on G layers for specific technical applications.

The reaction of pyridinium chlorochromate with furan to give enedione derivatives cannot be performed by using commercial PCC. Homemade and commercial PCC had different color and showed some differences in the XRD spectrum. XPS showed the presence of relevant amount of Cr(III) in the homemade reagent. DFT calculations showed that Cr(III) impurities in the reagent can catalyze the reaction with furan derivatives, if oxygen atom in the Cr(III) derivative attacks the furan ring, while it is reoxidized by PCC, through a migration of a chlorine atom.

The direct methane to methanol (MTM) oxidation is a grand challenge in catalysis, with profound economical implications for the modern chemical industry. Bioinspired metal-organic frameworks (MOFs) with active iron and copper sites have been emerging very recently as innovative catalytic platforms to accomplish the MTM conversion under mild conditions. This review discusses the current state of the art regarding the application of MOFs with iron and copper catalytic centers to perform the MTM reaction, with a focus on the diverse spectroscopic techniques used to unveil the electronic and structural properties of the MOF catalysts at a microscopic level. We explore the synthetic strategies employed to incorporate iron and copper sites into different MOF topologies, the efficiency and selectivity of the iron- and copper-bearing MOF catalysts, and the ensuing MTM reaction mechanisms proposed on the basis of spectroscopic characterization supported by theory. In particular, we evidence how the combination of complementary spectroscopic tools probing different regions of the electromagnetic spectrum is particularly useful to reach a satisfactory understanding of the key reaction pathways and intermediates. Finally, we provide a critical perspective on future directions to advance the use of MOFs to accomplish the MTM reaction.

The sepiolite/ZrO2 composites were prepared by sepiolite (Sep) modification with zirconium propoxide in toluene, at room temperature for 24 h (Sep –ZrI) or 95 °C for 4h (sample Sep –ZrII). The efficiency of the obtained adsorbents for the removal of phosphate from aqueous solutions at initial pH = 4 and pH = 8, was investigated. Characterization of the samples showed that higher temperature of synthesis for shorter time provided slightly higher content of amorphous Zr-phase, which was deposited on sepiolite fibers as a thin layer and agglomerated nanoparticles. Compared to Sep, the composites had lower point of zero charge and higher specific surface area and pore volume. The adsorption kinetics follows the pseudo second-order model. The adsorption capacities of the composites were approximately the same at both initial pH and higher at initial pH = 4 than at pH = 8. The XPS and ATR-FTIR of Sep-ZrI before and after adsorption identified the formation of inner-sphere complexes as the mechanism of phosphate adsorption. The slow release during desorption with NaOH solution confirmed strong bonds of phosphates with the surface of the composites.

The surface chemistry and the morphology of SnO2 nanowires, deposited by Vapour Phase Deposition (VPD) method on Au-covered silicon substrate, were studied before and after subsequent air exposure. For this purpose, surface-sensitive methods including X-ray Photoelectron Spectroscopy (XPS), Thermal Desorption Spectroscopy (TDS) and the Scanning Electron Microscopy (SEM) were applied. The studies presented within this paper allowed to determine the surface non-stoichiometry combined with the presence of carbon contaminations, in a good correlation with the surface morphology. The relative concentrations of the main components [O]/[Sn]; [C]/[Sn]; [Au]/[Sn] together with the O – Sn; O – Si bondings were analyzed. The results of TDS remained in a good agreement with the observations from XPS. Moreover, conclusions obtained for SnO2 nanostructures deposited with the use of Au catalyst were compared to the previous obtained for Ag-assisted tin dioxide nanowires. The information obtained within this studies are of great importance for the potential application of SnO2 nanowires deposited on Au covered Si substrate in the field of novel chemical nanosensor devices, since the results can provide an interpretation of how aging effects influence gas sensor dynamic characteristics.

Abstract: In the past years, lithium-ion solid-state batteries demonstrated significant advancements regarding such properties as safety, long-term endurance, and energy density. The properties of these depend on solid-state electrolytes and especially ionic transport interfacial transport with cathode or anode materials. Solid-state electrolytes based on lithium halides offer new opportunities due to their unique features such as broad electrochemical stability window, high lithium-ion conductivity, and elasticity at close to melting point temperatures that help to improve lithium-ion transport at interfaces. A comparative study of lithium indium halide (Li3InCl6) electrolytes syn-thesized by a mechano-thermal method using different optimization parameters revealed a signif-icant effect of ball-milling time, temperature, and pressure on lithium-ion transport. Based on the Electrochemical Impedance Spectroscopy (EIS) data in the temperature range of 25-100 °C, the optimized Li3InCl6 electrolyte phase demonstrates high ionic conductivity reaching 0.98 mS cm−1 at room temperature. However, at 70 °C, phase transformation was observed leading to significant changes in the activation energy for lithium-ion transport. In-situ X-ray diffraction and in-situ/operando X-ray photoelectron spectroscopy techniques confirmed the tempera-ture-dependent behavior of Li3InCl6 synthesized. These observations provide critical information for practical applications of solid-state electrolytes and nanocomposites based on Li3InCl6 within the broad temperature range for lithium-ion solid-state batteries with improved morphology, chemical interactions, and structural integrity.

High purity TiO2 and CuO powders were synthesized by the Pechini method, an inexpensive and easy-to-implement procedure to synthetize metal oxides. The variables of synthesis were the ethylene glycol:citric acid molar ratio and the pH. High reproducibility of the anatase and tenorite phase was obtained for all synthesis routes. The degree of purity of the powders was confirmed by XRD, FTIR, UV-vis absorption and XPS spectra. SEM and TEM images revealed the powders are composed by micrometer grains that can have a spherical shape (only in the TiO2) or formed by a non-compacted nanocrystalline conglomerate. FTIR spectra only vibrational modes associated to the TiO2 or CuO with a nanoparticle behavior. UV-vis absorption spectra revealed the values of maximum absorbance percentage of both systems are reached in the ultraviolet region, with percentages above 83 % throughout the entire visible light spectrum for the CuO system, a relevant result for solar cell applications. Finally, XPS experiments allow the observation of the valence bands and the calculation of the energy bands of all oxides.

In this paper, the phases in the Mg-Ti-O system using the 1:1 formulation of MgO:TiO2 mixing synthetic brucite of Mexican origin with TiO2 microparticles of high purity and with a heat treatment at 1100°C for 1 h were studied. The raw materials and formulation by XPS and DRX techniques were characterized. The results demonstrate the presence of different oxidation states in titania and the formation of different oxides in the Mg-Ti-O system when mixed and calcined at 1100°C; additionally, the formation of vacancies in the crystal lattice during the transformation from hexagonal brucite to magnesia with a cubic structure centered on the faces is estimated. With the results, its thermal behavior is warned based on the MgO-TiO2 phase diagram.

The performance of modified electrode of nanocomposite film consisting of polypyrrole-chitosan-titanium dioxide (Ppy-CS-TiO2) has been explored as non-enzymatic glucose biosensors. The synergy effect of TiO2 nanoparticles and conducting polymer on the current response of electrode resulted in higher sensitivity for nanocomposite modified electrode. The incorporation of TiO2 nanoparticles in the nanocomposite films were confirmed by XPS spectra. The FESEM and HR-TEM provided more evidences for the presence of TiO2 in Ppy-CS structure. Glucose biosensing properties were determined by amperommetry and cyclic voltammetry (CV) methods. The interfacial properties of nanocomposite electrodes were studied by electrochemical impedance spectroscopy (EIS). The developed biosensors showed a good sensitivity over the liner range of 1-14 mM with a detection limit of 614 μM for glucose. It also exhibited good selectivity and long term stability with no interference effect. The Ppy-CS-TiO2 nanocomposites film presented high electron transfer kinetics.

XPS and ARXPS characterization of surface layers resulting from the functionalization of polymers such as PVC modified with MPTMS and APTES is challenging due to the signals overlap, deriving both from the substrate and the functionalized layers. In this work, a freshly cleaved, ideally flat gold surface was used as carbon-free model substrate functionalized with MPTMS and subsequently grafted with APTES. Avoiding the overlap of signals from carbon atoms present in the substrate, the signals in the C1s, O1s, Si2p, S2p and N1s high-resolution spectra could be assigned to the MPTMS / APTES functionalized layer only and the curve fitting parameters could be determined. Quantitative analysis was in very good agreement with the expected stoichiometry of the functionalized layer, confirming the adopted curve fitting procedure. In addition, it was found that one molecule of APTES grafted two MPTMS via silane groups. ARXPS allowed determining the thickness of the functionalized layers: MPTMS thickness was found to be 0.5 (0.2) nm, MPTMS + APTES thickness 1.0 (0.2) nm in good agreement with Avogadro model calculations. This approach can be considered a powerful tool for characterising functionalized surfaces of more complex systems by XPS.

Silty clay modified by fly ash and crumb rubber is a kind of sustainable subgrade filler which has good anti-freeze-thaw resistance stability but wake vibration isolation performance. The objective of this study was to improve the vibration isolation of the modified soil and investigate the vibration isolation effect of the composite subgrade structure of XPS plates and the modified soil by indoor impact test. First, the vibration isolation performance of silty clay, modified soil and composite subgrade structure was respectively evaluated. Second, the effect of XPS plate’s thickness and vibration intensity on the vibration performance of the composite subgrade structure were evaluated. Third, the vibration isolation performance of the test groups under the condition of freeze-thaw cycles was assessed. The results show that the vibration isolation performance of subgrade can be effectively improved by setting XPS plates. The composite subgrade structure has certain vibration isolation effect, especially in vertical direction. Considering vibration isolation performance and costs, 5cm is the optimum XPS plates thickness. The composite subgrade structure has great vibration isolation performance under the condition of freeze-thaw cycles, so it is suitable to be applied in road subgrade in seasonal frozen regions.

Oxidation reactions on semiconducting metal oxides (SMOs) surfaces have been extensively worked on in catalysis, fuel cells, and sensors. SMOs engaged powerfully in energy-related applications such as batteries, supercapacitors, solid oxide fuel cells (SOFCs), and chemical gas sensors. The deep understanding of SMO surface and oxygen interactions and defect engineering has become significant because all those mentioned applications are based on the adsorption/absorption and consumption/transportation of adsorbed (physisorbed-chemisorbed) oxygen. More understanding of adsorbed oxygen and oxygen vacancies (〖V_O^•,V〗_O^(••)) is needed, as the former is the vital requirement for sensing chemical reactions, while the latter facilitates the replenishment of adsorbed oxygen ions on the surface. We determined the relation between sensor response (sensitivity) and the amounts of adsorbed oxygen ions (O_(2(ads))^-,O_((ads),)^- O_2(ads)^(2-),O_((ads))^(2-)), water/hydroxide groups (H2O/OH^-), oxygen vacancies (〖V_O^•,V〗_O^(••)), and ordinary lattice oxygen ions (O_lattice^(2-)) as a function of temperature. During hydrogen (H2) testing, the different oxidation states (W6+, W5+, and W4+) of WO3 were quantified and correlated with oxygen vacancy formation (〖V_O^•,V〗_O^(••)). We used a combined application of XPS, UPS, XPEEM-LEEM, and chemical, electrical and sensory analysis for H2 sensing. We established a correlation between the H2 sensing mechanism of WO3, sensor signal magnitude, the amount of adsorbed oxygen ions, and sensor testing temperature. This paper also provides a review of the detection, quantification, and identification of different adsorbed oxygen species. The different surface and bulk-sensitive characterization techniques relevant to analyzing the SMOs-based sensor are tabulated, providing the sensor designer with the chemical, physical, and electronic information extracted from each technique.

The variation of the cationic composition in I2-II-IV-VI4 semiconductor compounds is an effective tool for altering their properties in a controlled manner. In particular, a partial substitution of Cu for Ag in kesterite Cu2ZnSnS4 was proposed to suppress Cu-Zn antisite defects and the improve photovoltaic performance. However, the efficiency of this approach may substantially depend on the fabrication route. Here, we report on the synthesis of (Cu,Ag)-Zn-Sn-S (CAZTS) and Ag-Zn-Sn-S (AZTS) nanocrystals (NCs) by means of "green" chemistry in aqueous solution and their detailed characterization by Raman spectroscopy and by several complementary techniques. Through a systematic variation of the nominal composition and quantification of the constituent elements in CAZTS and AZTS NCs by XPS, we identified the vibrational Raman and IR fingerprints of both the main AZTS phase and secondary phases of Ag-Zn-S and Ag-Sn-S compounds (for the first time). The formation of the secondary phases of Ag-S and Ag-Zn-S cannot be avoided entirely for this type of synthesis. The Ag-Zn-S phase, having its bandgap in near infrared range, is the reason of the non-monotonous dependence of the absorption edge of CAZTS NCs on the Ag content, with a trend to redshift even below the bandgaps of bulk AZTS and CZTS.

In the current manuscript we assess to what extent X-ray photoelectron spectroscopy is a suitable tool for probing the dipoles formed at interfaces between self-assembled monolayers and metal substrates. To that aim, we perform dispersion-corrected, slab-type band-structure calculations on a number of biphenyl-based systems bonded to a Au(111) surface via different docking groups. In addition to changing the docking chemistry (and the associated interface dipoles), also the impacts of polar tail-group substituents and varying dipole densities are investigated. We find that for densely-packed monolayers the shifts of the peak positions of the simulated XP-spectra are a direct measure for the interface dipoles. In the absence of polar tail-group substituents they also directly correlate with adsorption-induced work-function changes. At reduced dipole-densities this correlation deteriorates, as work function measurements probe the difference between the Fermi-level of the substrate and the electrostatic energy far above the interface, while core level shifts are determined by the local electrostatic energy in the region of the atom from which the photoelectron is excited.

It is well known that fiber sizing is one of the most important component in the manufacturing of composites, and it does affect the mechanical properties including strength and stiffness. In this work, the influence of fiber sizing levels on the mechanical properties of carbon fibers (CF) is reported at room temperature by using single fiber tensile testing (Favimat+), single fiber pullout testing (SFPO), and interfacial elemental analysis using X-ray photoelectron spectroscopy (XPS). Standard modulus of CF (7±0.2 μm in diameter) were sized using two Michelman commercially available sizing formulations. The average solid content for each sizing formulation is 26.3 ± 0.2% and 34.1 ± 0.2%, respectively. HEXION RIMR 135 with curing agent RIMH 137 was used as a model thermoset epoxy matrix during the SFPO measurements. A predictive engineering fiber sizing methodology is also developed. Sizing amounts of 0.5, 1, and 2 wt. % on the surface of the fiber is achieved for both sizing formulations. For each fiber sizing level, 50 single fiber tensile testing experiments and 20 single fiber pull-out tests were conducted. The ultimate tensile strength (σult) of the carbon fibers and the interfacial shear strength (τ_app) of the single fiber composite were analyzed. it is also investigated the effect of the sizing levels on the interfacial shear stress and the O/C (Oxygen/Carbon) surface composition ratio. As a result, generalized fiber sizing and characterization methods were established. The developed methods can be used to characterize the strength and interfacial shear strength of any man-made fibers with different sizing formulations and solid contents, irrespective of the matrix i.e. thermoset or thermoplastic.

Electrochemical Promotion was used to modify the activity and selectivity of a Rh catalyst-electrode in the CO2 hydrogenation reaction. The experiments were carried out in a temperature range of 350-430οC at ambient pressure and at different CO2 to H2 gas feeding ratios (1:2 to 4:1). The only reaction products observed were CO and CH4, both under open and closed-circuit conditions. The CH4 formation rate was found to increase with both positive and negative potential or current application. The CO formation rate followed the opposite trend. The selectivity to CH4 increased under high values of hydrogen partial pressure and decreased at high pressures of CO2. The results demonstrate how Electrochemical Promotion can be used to finely tune activity and selectivity for a reaction of high technical and environmental importance.

: Sputtering of silicon in a Helium magnetron discharge (MS) has been reported as a bottom-up procedure to obtain He-charged silicon films (i.e. He nanobubbles encapsulated in a silicon matrix). The incorporation of heavier noble gases is demonstrated in this work with a synergistic effect producing increased Ne and Ar incorporations when using He-Ne and He-Ar gas mixtures in the MS process. Microstructural and chemical characterizations are reported by ion beam analysis (IBA) and scanning and transmission electron microscopies (SEM and TEM). In addition to gas incorporation, helium promotes the formation of larger nanobubbles. For the case of Ne high resolution X-ray photoelectron and absorption spectroscopies (XPS and XAS) are reported with remarkable dependence of the Ne 1s photoemission and the Ne K-edge absorption on the nanobubbles size and composition. The gas (He, Ne, Ar) charged thin films are proposed as “solid” targets for the characterization of spectroscopic properties of noble gases in a confined state without the need for cryogenics or high-pressure anvils devices. Also their use as targets for nuclear reaction studies is foreseen.

Modern surface analysis techniques are expanding significantly possibilities in description and attribution of historical artifacts. The present study is aimed to compare analytical ability of the X-ray fluorescent analysis (XRF) typically applied for studies ceramic art items with novel surface analysis methods: time-of-flight secondary ions mass spectroscopy (SIMS) and X-ray photoelectron spectroscopy (XPS) that were applied on measurements of elemental compositions of powder raw materials for porcelain fabrication: pegmatite P-1, Vesco-prima clay, kaolin, bone earth, dolomite, and feldspar. It was shown that SIMS successfully measures light elements unnoticeable for XRF such as lithium, beryllium, boron and heavy impurities not found out by XRF such as cobalt, cerium, copper, rubidium, vanadium. XPS has found thorium in the kaolin sample that was not detected by SIMS and XRF. The paper provides also values of chemical shifts of some XPS lines observed in materials under examination. The obtained information on relations of basic and impurity elements revealed by XRF and SIMS together with XPS chemical shifts data could be used to expose contemporary falsifications of historical porcelain and to attribute porcelain items during conservation process.