This study presents a straightforward electrochemical and plasma deposition method for producing Cobalt-doped Blue-TiO2 nanotubes with enhanced catalytic properties. After a titanium plate has been anodized, specific procedures are carried out that cause oxygen vacancies to form inside the TiO2 nanostructures. The obtained catalysts were subjected to electrochemical tests (to identify charge transfer resistance and flat band potential), optical analysis (to determine the band gap and Urbach energy) and also characterized in terms of morphology, wettability and antibacterial effect in order to understand and analyze the impact of the Co doping method on the final catalyst characteristics. A hydrophilic film with star-shaped structures and with antibacterial effect was created when cobalt was electrochemically doped to Blue-TiO2 nanotubes. By using this electrochemical doping technique, the Urbach energy was raised from 1.171 to 3.836 eV while the band gap energy was decreased from 3.04 to 2.88 eV. Additionally, photodegradation experiments using artificial doxycycline (DOX) water were conducted to determine the practical relevance of the research findings. In areas like antimicrobial applications and photodegradation of DOX, these extra experiments aimed to show the practical applicability and potential advantages of the research findings.

We report on the successful preparation of wet dressings hydrogels based on Chitosan-Poly(N-Vinyl-Pyrrolidone)-Poly(ethylene glycol)-Poly(acrylic acid) and Poly(ethylene oxide) by e-beam cross-linking in weakly acidic media, to be used for rapid healing and pain release of infected skin wounds. The structure and compositions of hydrogels investigated according to sol-gel and swelling studies, network parameters, as well as FTIR and XPS analyses showed the efficient interaction of the hydrogel components upon irradiation, maintaining the bonding environment while the cross-linking degree increasing with the irradiation dose and the formation of a structure with the mesh size in the range 11-67 nm. Hydrogels with gel fraction above 85% and the best-swelling properties in different pH solutions were obtained for hydrogels produced with 15 kGy. The hydrogels are stable in the simulated physiological condition of an infected wound and show appropriate moisture retention capability and the water vapor transmission rate up to 272.67 g m-2 day-1, to ensure fast healing. The hydrogels proved to have a significant loading capacity of ibuprofen (IBU), being able to incorporate a therapeutic dose for the treatment of severe pains. Simultaneously, IBU was released up to 25% in the first 2h, having a release maximum after 8h.

The corrosion resistance of two cast CoCr based alloys, with different amounts of chromium and with different alloying elements in the bulk composition of the alloy, was assessed. Herewith, we investigated the corrosion behavior of Co21Cr8Mo7W and Co29Cr7W by open circuit potential (OCP), potentiodynamic polarization (PP) and electrochemical impedance spectroscopy (EIS) in 0.1 M phosphate buffer solution (PBS) at 37°C for long time immersion. After 1000 hours of immersion, the corrosion current density (icor), estimated from anodic polarization tests, is lower for Co21Cr8Mo7W (i.e. 49 nA cm-2) alloy compared to Co29Cr7W alloy (180 nA cm-2). As regards the corrosion potential (Ecor), a nobler value was observed for Co21Cr8Mo7W (i.e. -59 mV vs. Ag/AgCl) compared to Co29Cr7W (i.e. -114 mV vs. Ag/AgCl). These findings suggest a better corrosion resistance of the film formed on the alloy containing lower amount of Cr and two alloying elements, namely Mo and W. These results are promising ones in terms of medical applications because they open new strategies in obtaining alloys with lower content of chromium and with higher protective properties against corrosion attack.