The global development of bioeconomy is impossible without technologies for comprehensive processing of plant renewable resources. The use of proven pretreatment technologies raises the possibility of industrial implementation of enzymatic conversion of polysaccharides from lignocellulose considering the process complexity. For instance, a well-tuned kraft pulping produces a substrate easily degraded by cellulases and hemicelulases. Enzymatic hydrolysis of bleached hardwood kraft pulp was carried out using an enzyme complex of endoglucanases, cellobiohydrolases, b-glucosidases and xylanases produced by recombinant strains of Penicillium verruculosum at a 10 FPU/g mixture rate and a 10 % substrate concentration. As a result of biocatalysis the following products are obtained: sugar solution, mainly glucose, xylobiose, xylose, as well as other minor reducing sugars; modified complex based on cellulose and xylan. The composition of biomodified kraft pulp was determined involving the use of HPLC. The method for determining the degree of crystallinity on an X-ray diffractometer was used to characterize the properties. The article shows the possibility of producing modified cellulose cryogels by amorphization with concentrated 85 % H3PO4 followed by precipitation with water and supercritical drying. Analysis of the enzymatic hydrolysate composition reveals the predominance of glucose (55...67 %) in reducing sugars with a maximum content of up to 6 % in the solution after 72 hours. The properties and structure of modified kraft pulp were shown to change during biocatalysis, in particular, the degree of crystallinity increased by 5 % after 3 hours of enzymatic hydrolysis. We obtained cryogels based on the initial and biomodified kraft pulp with conversion rates of 35, 50 and 70 %. The properties of these cryogels are not inferior to those based on industrial microcrystalline cellulose, as confirmed by the specific surface area, degree of swelling, porosity and SEM images. Thus, kraft pulp enzymatic hydrolysis offers prospects not only for producing sugar-rich hydrolysates for microbiological synthesis, but also for producing cellulose powders and cryogels with specified properties.

Sulfite and kraft pulping are two principal methods of industrial delignification of wood. In recent decades, those have been considered as possibilities to pretreat recalcitrant wood lignocellulosics for enzymatic hydrolysis of polysaccharides and subsequent fermentation of obtained sugars to valuable bioproducts. Current work compares chemistry and technological features of two different cooking processes in the preparation of polysaccharide substrates for deep sacchari-fication with P. verruculosum glycosyl hydrolases. Bleached kraft and sulfite pulps were subjected to hydrolysis with enzyme mixture of high xylanase, cellobiohydrolase and β-glucosidase activities at a dosage of 10 FPU/g of dry pulp and fiber concentration of 2.5, 5 and 10%. HPLC was used to analyze soluble sugars after hydrolysis and additional acid inversion of oligomers to monosaccharides. Kraft pulp demonstrated higher pulp conversion after 48 h (74-99%), mostly resulted from deep xylan hydrolysis. Sulfite-pulp hydrolysates, obtained in similar conditions, due to higher hexose concentration (more than 50 g/L), had higher fermentability for industrial strains producing alcohols, microbial protein or organic acids. Along with saccharification, enzymatic modification of non-hydrolysed residues occurred, which led to decreased degree of polymerization and composition changes in two industrial pulps. As a result, crystallinity of kraft pulp increased by 1.3%, which opens possibilities for obtaining new types of cellulosic products in pulp and paper industry. The high adaptability and controllability of enzymatic and fermentation processes creates prospects for the modernization of existing factories.