Zn–Ni plating is indispensable in various industries because of its high corrosion resistance. However, Ni has been reported to trigger allergies; thus, an alternative Ni-free plating is desired. Zn–Fe plating is considered to be a promising candidate, albeit its corrosion resistance still needs to be improved. The corrosion resistance of Zn–Fe plating is expected to increase by the addition of Mo as the third alloying element as it is more noble than Zn and Fe. In this study, Zn–Fe–Mo plating with a corrosion resistance nearly equivalent to that of the Zn–Ni plating was fabricated. Zn–Fe–Mo plating was electrically deposited from continuously agitated plating baths prepared by mixing ZnSO₄, FeSO₄, Na₂MoO₄, Na₃C₆H₅O₇, and Na₂SO₄ using Fe or Ni plates as the substrate. The surface morphology, composition, crystal phase, and electronic state of Mo of the platings were investigated by SEM-EDS, XRD, and XPS. The anti-corrosion performance was evaluated by Tafel extrapolation method. Formation of plating comprising a Mo containing alloy phase was found to be crucial for improving corrosion resistance. The Zn–Fe–Mo plating demonstrates promise for replacing anti-corrosion Zn–Ni platings.

Carbonous nanomaterials are promising additives for composite coatings for heat-dissipation materials because of their excellent thermal conductivity. Here, copper/carbonous nanomaterial composite coatings were prepared using nanodiamond (ND) as the carbonous nanomaterial. The copper/ND composite coatings were electrically deposited onto copper substrates from a continuously stirred copper sulfate coating bath containing NDs. NDs were dispersed by ultrasonic treatment, and the initial bath pH was adjusted by adding sodium hydroxide solution or sulfuric acid solution before electrodeposition. The effects of various coating conditions—the initial ND concentration, initial bath pH, stirring speed, electrical current density, and the amount of electricity—on the ND content of the coatings were investigated. Furthermore, the surface of the NDs was modified by hydrothermal treatment to improve ND incorporation. A higher initial ND concentration and a higher stirring speed increased the ND content of the coatings, whereas a higher initial bath pH and a greater amount of electricity decreased it. The electrical current density showed a minimum ND content at approximately 5 A/dm². Hydrothermal treatment, which introduced carboxyl groups onto the ND surface, improved the ND content of the coatings. A copper/ND composite coating with a maximum of 3.85 mass% ND was obtained.

: Since the COVID-19 pandemic, people have become aware that materials (products) can transmit infection and have begun to focus on questions such as how bacteria and germs, the sources of in-fection, maintain their infectivity on material surfaces, and the extent to which materials can or cannot prevent this. and to what extent materials can and cannot prevent it. The SIAA, a non-profit organization of many Japanese companies, had created an entirely separate interna-tional standard for materials' antibacterial, antiviral, and antibiofilm properties (products). The authors have studied the academic basis for the operation of the standards and were deeply in-volved as researchers in establishing one of the standards. This paper describes the interna-tional standards and some representative examples of the authors' actual use of these standards and explains the current status and future problems.

An influenza A virus (H3N2) with an envelope with the same structure as COVID-19 was used for antiviral testing of material surfaces, in comparison with some results of feline calicivirus. The evaluation method used was the film adhesion method, in which the virus solution is placed on the material and adhered to it using a film. The evaluation method was based on the film adhesion method, in which the virus solution is placed on the material and adhered with a film, and the plaque method, in which the cell virus is allowed to infect the material and form plaques, but the appropriate virus concentration must be adjusted to observe the plaques. When not under that restriction, the plaques are often incomplete; this is observed. For this reason, this study applied an area measurement method that can reflect viral activity even when plaques are not obtained. This study revealed that different types of metallic materials have different antiviral properties. Specifically, the antiviral activity of iron, carbon steel, and nickel was relatively high, while that of stainless steel and titanium was relatively low. The order of antiviral activity was as follows: Fe, SS400, Ni, SUS316L, SUS304, and Ti.