Titanium micro-scale topography results in excellent osteoconductivity and bone-implant integration. However, the biological effects of sub-micron topography are unknown. We compared osteoblastic phenotypes and in vivo bone and implant integration abilities between titanium surfaces with micro- (1–5 µm) and sub-micro-scale (0.1–0.5 µm) topographies and machined titanium. Average roughness was 12.5 ± 0.65 nm, 123 ± 6.15 nm, and 24 ± 1.2 nm for machined, micro-rough, and sub-micro-rough surfaces, respectively. The micro-rough surface showed the fewest cells attaching during the initial stage and the lowest proliferation. Calcium deposition and expression of osteoblastic genes were highest on the sub-micro-rough surface and lowest on the machined surface. Bone-to-implant integration was strongest for the micro-rough surface, consistent with it having the greatest ability to retain cells in vitro. Thus, the biological effects of titanium surfaces are not necessarily proportional to the degree of roughness in osteoblastic cultures or in vivo. Sub-micro-rough titanium ameliorates the disadvantage of micro-rough titanium by restoring cell attachment and proliferation and enhances the rate of osteoblastic differentiation over that of micro-rough titanium; however, bone integration and the ability to retain cells are compromised due to its lower interfacial mechanical locking compared to that of micro-rough titanium.

Friction is an important subject for sustainability due to problems associated with energy loss. Recent years, surface micro- and nanostructures have attracted much attention to reduce friction; however, suitable structures are still under consideration. Many functional surfaces are present in nature, such as the friction reduction surfaces of snake skins. In this study, we focused on firebrats, Thermobia domestica, living in narrow spaces such as under bark, so their surface frequently contacts with surrounding surfaces. We speculate that their body surface would be adapted to reduce friction. To investigate the firebrat surface functions, firebrat surfaces were observed by using a field-emission scanning electron microscope (FE-SEM) and a colloidal probe atomic force microscope (AFM), respectively. Results of surface observations by the FE-SEM revealed that firebrats are entirely covered with scales, whose surfaces have micro groove structures. Scale groove periods around the firebrat's head are almost uniform within a scale but vary between scales. AFM friction force measurements revealed that firebrat scale reduces friction by decreasing contact area between scales and a colloidal probe. The heterogeneity of groove periods of the scales suggest that it is difficult to fix the whole body in particular rough surfaces and that lead to be "fail-safe".