One of the modern methods of improving operating characteristics of titanium and titanium-based alloys under conditions of friction and increased contact loads is the method of ion-plasma nitriding. The effect of nitriding of VT5 alloy (Al 4,5-6,7 %, V to 1,2 %, Mo to 0,8 % − analogue 3.7115) in the plasma of a glow discharge excited in a hollow cathode on its tribological characteristics in pairs with different materials in T-1 fuel and under dry friction conditions has been studied. For research and tribological tests, samples of VT5 alloy were nitrided in the plasma of a glow discharge excited in a hollow cathode at a temperature of 975 ± 15°C and a pressure of 58 ± 2 PA in a nitrogen-argon gas mixture with a nitrogen content of 78 %. Studies of samples of VT5 alloy after nitriding showed that the surface roughness Ra was in the range of 0.58-0.64, and the surface hardness HV5 was 525 ± 20 kgf/mm² at a base hardness of 325 ± 15 kgf/mm². Tribological tests were performed on a friction machine 2070 SMT-1 according to the scheme "cube - roller". Tests under conditions of friction with oil were performed at a load of 200 N. The sliding speed during the tests was 1.3 m/s, the test time was 75 sec. The test under dry friction conditions was carried out at a load of 100 N and a sliding speed of 0.785 m/s, the test time was 30 minutes. Low wear ability in relation to the nitrided titanium alloy VT5 (<2.4x10^-4 mm³/s), as well as friction coefficients at the level of 0.08 to 0.12 in the order of their growth had bronze VB-23NTS (Pd 18–22 %, Ni 3–4 %, Zn 3–4 %, Sb 3–4 %, P 0.15–0.3) r.O10C2N3, VB-24 (Sb 4.7–6, 2 %, P 0.4–0.9), steel 1.3505, cast iron GGG80, cemented steel 20Cr3MoWV.

Experimental studies on the development of processes of obtaining ultradispersed metal-ceramic materials and coatings Mo-ZrO₂, Mo-Al₂O₃, W-ZrO₂, W-Al₂O₃ CVD by deposition from the gas phase in CO₂ process using low-temperature nonequilibrium plasma were carried out.The structure, microhardness, phase composition, and high-temperature annealing behavior of the materials were studied. It is shown that the choice of parameters of the deposition process and temperature annealing can be controlled by the distribution function of ultradispersed particles in the material and their sizes.High-temperature X-ray studies of "molecular" two-phase alloys Mo- Al₂O₃ and Mo- ZrO₂show that, depending on the elastic and thermal properties of the matrix materials and dispersed particles, the molybdenum matrix can be in an all-round tensed or all-round compressed state.In the study of the electro-physical characteristics of the two-phase disperse-strengthened alloys Mo- ZrO₂, Mo- Al₂O₃, W- ZrO₂, W- Al₂O₃ it has been established that in the region of temperatures 1023...1273K anomalous changes of specific electrical resistance and instability of thermal eddy in magnitude are observed apparently connected with the presence of internal stresses in material caused by ultradisperse particles.Theoretical aspects of the problem of increasing the carriers density in nanocomposite materials are reviewedTheoretical analysis of the effect of the ensemble of microparticles on the change of electron density in ultradisperse metal-ceramic materials is carried out. It is shown that the average values of the electron density in the matrix with the introduction of 1% of particles with a radius of 50 A increase by more than two orders of magnitude.The possibilities of creating ultradisperse compositions using radiation-plasma methods are considered.