Biodegradable poly(ɛ-caprolactone) (PCL) and its composites or blends have gotten a lot of attention in the last decade because of their potential applications in human life and environmental remediation. As a result, there is a growing interest in the synthesis of PCL-composites/blends and their applications. Greater efforts have been made to develop biodegradable chemical materials as adsorbents that do not pollute the environment in order to replace traditional materials. Among the numerous types of degradable materials, PCL is currently the most promising, the most popular, and the best material to be developed, and it is referred to as the "green" eco-friendly material. Membranes and adsorbents for water treatment, packaging and compost bags, controlled drug carriers, biomaterials for tissues such as bone, cartilage, ligament, skeletal muscle, skin, cardiovascular and nerve tissues are just some of the applications of this biodegradable polymer (PCL). The goal of this review is to present a brief overview of PCL, its properties, syntheses of PCL, PCL composites, and PCL blends, but to provide a detailed investigation into the utility of PCL/PCL-based adsorbing agents in the removal of dyes/heavy metal ions.

The structure of wound dressing materials presents one of the most relevant characteristics for effective skin tissue repair. Electrospinning is a common technique used to produce polymeric fibres that can mimic fibrillar disposition of skin extracellular matrix, favouring cell migration, and thus regeneration of the damaged tissue. Moreover, beads, also known as by-products of electrospinning, have potential as reservoirs for sustained drug release. Processing parameters, such as molecular weight and viscosity of the polymer solution, can affect the desirable morphologies of electrospun films. Thereby, this work had the purpose of producing and characterized electrospun polycaprolactone (PCL) mats loaded with propolis, a popular extract in traditional medicine with potential for skin repair aid. Films with different morphologies were obtained depending on the storage period of the solution prior to the lectrospinning, probably due to the PCL hydrolysis. FTIR analyses of the extract confirmed propolis composition. GPC and viscosity analyses demonstrated that the decrease in molar mass over the storage period was responsible for nanostructure diversity. Propolis acts as a lubricant agent, affecting the spun solutions' viscosity and the thermal properties and hydrophilicity of the films. All films are within the value range of the water vapour transpiration rate of the commercial products. The presence of beads did not affect the propolis release pattern. However, "in vitro" wound healing assay showed that propolis-loaded films composed by beaded fibres increased the cell migration process. Thus, it can be inferred that these films presented the potential for wound dressing application.

Paclitaxel is a natural, highly lipophilic anti proliferative drug widely used in medicine. We have studied the release of tritium-labeled paclitaxel (³H-PTX) from matrices destined for the coating of vascular stents and produced by the electrospinning method from the solutions of polycaprolactone (PCL) with paclitaxel (PTX) in hexafluoisoropropanol (HFIP) and/or solutions of PCL with PTX and human serum albumin (HSA) in HFIP or HIFP-dimethyl sulphoxide (DMSO) blend. The release of PTX has been shown to depend on the solvent and the composition of electrospinning solution, as well as the composition of the surrounding medium, particularly the concentration of free PTX and PTX-binding biomolecules present in human serum. It was shown that 3D matrices can completely release PTX without weight loss. Two-phase PTX release from optimized 3D matrices was obtained: ~27% of PTX was released in the first day, another 8% were released over the next 26 days. Wherein ~2.8%, ~2.3%, and ~0.25% of PTX was released on day 3, 9, and 27, respectively. Considering PTX toxicity, the rate of its diffusion through the arterial wall, and the data obtained the minimum cytostatic dose of the drug in the arterial wall will be maintained for at least three months.

Cell-based therapies and tissue engineering applications require biocompatible substrates that support and regulate the growth, survival, and differentiation of specific cell types. Extensive research efforts in regenerative medicine are devoted to the development of tunable biomaterials which support various cell types including stem cells. In this research, the non-cytotoxic biopolymer polycaprolactone (PCL) was fabricated into 2D and 3D scaffolds with or without the low-pressure oxygen plasma treatment to enhance hydrophilicity. Cellular responses and biocompatibility were evaluated using a human Wharton’s jelly mesenchymal stem cell line (BCP-K1). The 2D PCL scaffolds enhanced initial cell attachment compared to the 3Ds indicated by a higher expression of focal adhesion kinase (FAK). Whilst, the 3D scaffolds promoted cell proliferation and migration as evidenced by higher cyclin A expression and filopodial protrusion, respectively. The 3D scaffolds potentially protected the cell entering to apoptosis/necrosis program and induced cell differentiation, evaluated by gene expression. Both 2D and 3D PCL appeared to have stronger effects on cell behavior than a control substrate (polystyrene). In summarize, the different configuration and surface properties of PCL scaffolds provide various options for modulation of stem cell behaviors, including attachment, proliferation, survival, and differentiation, when combined with specific growth factors and culture conditions.

Additive manufacturing or 3D printing applying polycaprolactone-(PCL)-based medical devices represents an important branch of tissue engineering, where the sterilization method is a key process for further safe application in vitro and in vivo. In this study, the authors intend to access the most suitable gamma radiation conditions to sterilize PCL-based scaffolds in a preliminary biocompatibility assessment, envisioning future studies for airway obstruction conditions. Three radiation levels were considered, 25 kGy, 35 kGy and 45 kGy and evaluated as to their cyto- and biocompatibility. All three groups presented biocompatible properties, indicating an adequate sterility condition. As for the cytocompatibility analysis, devices sterilized by 35 kGy and 45 kGy showed better results, with the 45 kGy showing overall improved outcomes. This study allowed to select the most suitable sterilization condition for PCL-based scaffolds, aiming at immediate future assays, by applying 3D-customized printing techniques to specific airway obstruction lesions of the trachea.

Plantago major L. is a worldwide available plant that has been used traditionally for several medical application due to its properties such as wound healing, anti-inflammatory, antimicrobial etc. This work aimed to develop and evaluate nanostructured PCL electrospun dressing with P. major extract encapsulated in nanofibers for application in wound healing. The extract from leaves was obtained by extraction in a mixture of water:ethanol= 1:1 of the freeze-dried extract presented a minimum inhibitory concentration (MIC) for Staphylococcus Aureus susceptible and resistant to methicillin of 5.3 mg/mL, a high antioxidant capacity, but a low content of total flavonoids. Electrospun mats without defects were successfully produced using two P. major extract concentrations based on MIC value. The extract incorporation in PCL nanofibers was confirmed by FTIR and contact angle measurements. The PCL/P. major extract was evaluated by DSC and TGA demonstrating that incorporation of the extract decreases the thermal stability of the mats as well as the degree of crystallinity of PCL-based fibers. The P. major extract incorporation on electrospun mats produced a significant swelling degree (more than 400%) and increased the capacity of adsorbing wound exudates and moisture, important characteristics for skin healing. The extract-controlled release evaluated by in vitro study in PBS (pH, 7.4) shows that P. major extract delivery from the mats occurs in the first 24 h, demonstrating their potential capacity to be used in wound healing.

Electrospun ultrathin fibers based on binary compositions of polylactide (PLA) and poly(ε-caprolactone) (PCL) with different ratios of polymer components from 0/100 to 100/0 wt. % were studied. Using a combination of thermal (DSC) and relaxation (EPR) measurements, the effect of biopolymers content on the characteristics of the crystal structure of PLA and PCL and the diffusive rotational mobility of the stable TEMPO radical in the amorphous regions of PLA/PCL compositions was shown. It was revealed that after PLA and PCL blending, significant changes in the degree of crystallinity of PLA, PCL segmental mobility, sorption capacity of the radical as well as activation energy of rotational diffusion in the amorphous regions of PLA/PCL composition are observed. The characteristic region of biopolymers’ composition from 50/50 to 30/70 % PLA/PCL blends ratio was found, where the inversion transition of PLA from dispersive medium to dispersive phase where an inversion transition is assumed when the continuous medium of the PLA transforms into a discrete phase. The performed studies made it possible for the first time to carry out a comprehensive analysis of the effect of the system component ratio on the structural and dynamic characteristics of the PLA/PCL film material at the molecular level.

Bone tissue engineering has been developed in the past decades, with the engineering of bone substitutes on the vanguard of this regenerative approach. PCL based scaffolds are fairly applied for bone regeneration, and several composites have been incorporated, as to improve the devices’ mechanical properties and tissue ingrowth. In this study, HA was incorporated on PCL based scaffolds with two different proportions, 80:20 and 60:40. Devices were produced with two different techniques, SC and MB, and further investigated with regards to their mechanical characteristics and in vitro cytocompatibility. Results show the MB devices to present more promising mechanical properties, along with the incorporation of HA. The latter is also related to an increase in osteogenic activity and promotion. Overall, this study suggest PCL:HA scaffolds to be promising candidates for bone tissue engineering, particularly when produced by the MB method.

Large volume bone defect regeneration is complex and demands time to complete. Several regeneration phases with unique characteristics including immune responses follow, overlap, and interdepend on each other and, if successful, lead to the regeneration of the organ bone's form and function. However, during traumatic, infectious, or neoplastic clinical cases, the intrinsic bone regeneration capacity may exceed, and surgical intervention is indicated. Scaffold-guided bone regeneration (SGBR) has recently shown efficacy in preclinical and clinical studies. To investigate different SGBR strategies over periods of up to 3 years we have established a well characterized large segmental tibial bone defect ovine model, for which we have developed and optimized immunohistochemistry (IHC) protocols. We present an overview of the immunohistochemical characterization of different experimental groups in which all ovine segmental defects were treated with a bone grafting technique combined with a three-dimensionally printed medical-grade polycaprolactone-tricalcium phosphate (mPCL-TCP) scaffold. The qualitative data set is based on osteoimmunological findings gained from IHC analyses of over >350 sheep surgeries over the past two decades. Our systematic and standardized IHC protocols enabled us to gain further insight into the complex and long-drawn-out bone regeneration processes, which ultimately proved to be a critical element for successful translational research.

This experimental study examined the application effect of polycaprolactone (PCL), an organic resin material with excellent elasticity and ductility, on improving the mechanical performance of cellulose nanocrystal (CNC) cement composites. To analyze the effect, a test specimen containing CNC and PCL mixed, containing only CNC, and a control (plain) specimen containing nothing were compared. PCL was compared according to its shape, and in the case of Granules, which is the basic shape, interfacial adhesion with cement was not achieved, so a DCM solution was used to dissolve and use the Granules form. As a method for bonding PCL to the CNC surface, the CNC surface was modified using 3-aminopropyltriethoxysilane (APTES), and surface silylation was confirmed through Fourier transform infrared spectroscopy(FT-IR) analysis. To evaluate the dispersibility according to the application of PCL to the modified CNC, particle size analysis (PSA) and zeta potential analysis were performed according to the PCL mixing amount (0.1, 0.3, 0.5, and 1 vol.% compared with those of CNC) and size distribution. Through the zeta potential value, the highest dispersion stability was shown at 1 vol.%. The cohesive force of CNC was low and the dispersion stability was high according to the application of PCL. According to the results of the dispersion stability evaluation, the degree of hydration of the dissolved PCL 1 vol.%, CNC-only specimens, and plain specimens were analyzed. Hydration products increased by increasing the degree of hydration in the unhydrated area. However, the incorporation of PCL showed a low degree of hydration, and the analysis of strength characteristics also showed a decrease of approximately 27% compared with that of plain specimens. This was because the bonding with SiO2 was not smooth owing to the solvent, thus affecting internal hydration. To investigate the effect of the PCL shape, the compressive and flexural strength characteristics were compared using PCL powder as an additional parameter. The compressive and flexural strength values were improved by approximately 54% and 26%, respectively, compared with those of the plain specimen. Scanning electron microscopy (SEM) analysis determined that the filler effect that made the micropore structure denser, affected the mechanical performance improvement.

Notwithstanding the advances achieved in the last decades in the field of synthetic bone substitutes, the development of biodegradable 3D scaffolds with ideal mechanical and biological properties remains an unattained challenge. In this work, a novel approach is explored to produce synthetic bone grafts mimicking the complex bone structure using additive manufacturing. For the first time, scaffolds were produced, using an extrusion technique, composed of a thermoplastic polymer, polycaprolactone (PCL), hydroxyapatite nanoparticles (HANp), and polyethylene glycol diacrylate (PEGDA). These scaffolds were further compared with two groups of scaffolds: one composed of PCL and another of PCL and HANp. After production, optimisation and characterisation of these scaffolds, an in vitro evaluation was performed using human dental pulp stem/stromal cells (hDPSCs). Through the findings it was possible to conclude that PEGDA scaffolds were successfully produced presenting networks of interconnected channels, presenting hydrophilic properties (15.15 4.06°), adequate mechanical performance (10.41MPa 0.934), and allowing a cell viability significantly superior to the other groups analysed. To conclude, findings in this study demonstrated that PCL, HANp and PEGDA scaffolds may have promising effects on bone regeneration and might open new insights for 3D tissue substitutes.

The structural evolution and phase composition of multi-block thermoplastic polyurethanes, with different nature of the soft segments based on poly(butylene adipate) (PBA), were analyzed during in-situ thermal treatments. A combination of synchrotron small- and wide-angle X-ray scattering, differential scanning calorimetry, thermogravimetric analysis, and FTIR spectroscopy was used to determine the influence of macrodiol nature and crystallization conditions on the polymorphic behavior of PBA. Using a new synthesis scheme, a relatively high degree of crystallinity for urethane blocks was achieved, which depends on the diisocyanate type in the structure of the soft segment. The hard segment domains impose geometrical constraints on PBA, thereby altering its crystallization process compared to the neat oligomer. Thus, crystallization after annealing at a low temperature (80 °C) is fast, predominantly yielding a metastable β-phase. When heated to 180 °C, which is higher than the hard-segment melting temperature, a phase-separated structure is observed. Subsequent crystallization is slower, favoring the formation of the stable α-PBA modification. The phase separation can be observed even after the hard block melting. A notably slow crystallization from an isotropic melt was documented after the disruption of phase separation at 230 °C.