The aim of this study was to analyse the biocompatibility of a material based on lactic acid (PLA)/polyhydroxybutyrate(PHB)/thermoplastic starch (TPS) in combination with additives (plasticizers: acetyltributyl citrate (ATBC) and oligomeric lactic acid ( OLA)). Three types of materials were tested: I: PLA/PHB/TPS + 25% OLA, II: PLA/PHB/TPS + 30% ATBC, III: PLA/PHB/TPS + 30% OLA. The 3D printing itself was preceded by the creation of filaments from granulate and the design of samples. A filament production machine – Composer 450 (3devo; The Netherlands) was used to produce the filaments. Experimental samples were produced by FDM technology on a 3D printer DeltiQ2 (Trilab, Czech Republic). The evaluation of the biocompatibility of the materials included cytotoxicity tests such as the monitoring of viability, proliferation, morphology of cells, and their settlement on the surface of the materials. The cell line 7F2 osteoblasts (Mus musculus) was used in the experiments. Based on the tests, results confirmed the significant influence of plasticizers and their proportions in the mixtures. PLA/PHB/ATBC + 25% OLA was evaluated as the optimal material for biocompatibility with 7F2 osteoblasts. The tested biomaterials have the potential for further investigation, with a possible change in the proportion of the plasticizer, which has a fundamental impact on their biological properties.

The environmental exposure of human in the daily and occupational activities to plasticizers may adversely affect human health, and thus represents a global issue. The altered expression of MicroRNAs (miRNAs) exerts an important pathogenic role linked also to the exposure to plasticizers. This systematic review summarizes the recent findings showing modified ex-pression of miRNAs in cancer due to plasticizers exposures. Following Preferred Reporting Items for Systematic Reviews and Meta-Analyses (PRISMA) methodology, we performed a systematic review of the past ten years, focusing on the relationship between plasticizer exposures and expression of miRNAs cancer. Starting by 535 records, 17 articles were included. Results support the hypothesis that exposure to plasticizers cause changes or deregulation of a number of oncogenic miRNAs and showed that plasticizers interaction with several redundant miRNAs, such as let-7f, let-7g, miR-125b, miR-134, miR-146a, miR-22; miR-192, miR-222, miR-26a, miR-26b, miR-27b, miR-296, miR-324, miR-335, miR-122, miR-23b, miR-200, miR-29a and miR-21, might induce deep alterations. These genotoxic and oncogenic responses can eventually lead to abnormal cell signaling pathways and metabolisms that participate in many overlapped cellular processes, and miRNA level changes can be a useful tool for the toxicological assessment of environmental pollutants, including plastic additives and plasticizers

The consideration toward Waste Cooking Oils (WCOs) is changing from hazardous waste to valuable raw material for industrial application. During the last five years some innovative processes based on the employment of recycled WCO have appeared in the literature. In the present review article, the most recent applications of recycled Waste Cooking Oil are reported and discussed. These include the production of bio-plasticizers, the application of chemicals derived from WCOs as energy vectors, and the use of WCOs as solvent for pollutant agents.

Global use of single-use non-biodegradable plastics, like bottles made of polyethylene tereph-thalate (PET), have contributed to catastrophic levels of plastic pollution. Fortunately, microbi-al communities are adapting to assimilate plastic waste. Previously, our work showed a full consortium of five bacteria capable of synergistically degrading PET. Using omics approaches we identified key genes implicated in PET degradation within the consortium’s pangenome and transcriptome. This analysis led to the discovery of a novel PETase, EstB, discovered to hydrolyze oligomer BHET, and polymer PET. Besides genes implicated in PET degradation, many other biodegradation genes were discovered. Over 200 plastic and plasticizer degrada-tion related genes were discovered through the Plastic Microbial Biodegradation Database (PMBD). Diverse carbon source utilization was observed by a microbial community-based as-say, which paired with an abundant number of plastic and plasticizer degrading enzymes in-dicates a promising possibility for mixed plastic degradation. Using RNAseq differential analysis, several genes were predicted to be involved in PET degradation including aldehyde dehydrogenases and several classes of hydrolases. Active transcription of PET monomer me-tabolism was also observed, including the generation of polyhydroxyalkanoate (PHA) bi-opolymers. These results present an exciting opportunity for the bio-recycling of mixed plastic waste with upcycling potential.

Honey is a sweet substance extensively consumed in the world for its nutritional and healthy properties. However, residues of pesticides and environmental contaminants can compromise its quality. For this reason, the physicochemical parameters, and the organic contamination of monofloral and multifloral honeys from three regions of Algeria (Tiaret, Laghouat and Tindouf) were monitored to evaluate the quality of honey and the safety for consumers. In general, the results obtained from the physicochemical analyses were in line with the EU standards. In terms of contamination, pesticides authorised and used in Algerian agriculture (matalaxyl-M and cyromazine), as well as banned pesticide (carbaryl), were found in almost all the samples. However, only the concentration of cyromazine was higher than the relative EU maximum residue levels. PCB 180, PCB 189, anthracene, fluorene and phenanthrene were mainly detected. All the honeys show traces of DiBP, DBP, DEHP and DEHT, but no traces of bisphenols were found. Moreover, the dietary exposure assessment shows that a small amount of Algerian honey can be safely consumed. Overall, data from this study should motivate the Algerian government to enhance their monitoring activities in beekeeping and to find solutions for implementing more sustainable agricultural practices harmonizing with the international legislation.

Poly(vinyl acetate) (PVAC) is a ubiquitous polymer in various industrial applications, including paints and adhesives. While extensive research has focused on understanding the degradation mechanisms of PVAC-based paint, under different environmental conditions, limited attention has been paid to the long-term stability of PVAC-based white glues, especially when used in artworks. This study investigates the accelerated degradation of a commercial PVAC-based white glue considered as representive of this class of materials as used in contemporary artworks, to predict its durability and assess its behavior in art objects. Through accelerated aging experiments and comparison with natural aging observed in artworks, the study reveals the formation of chromophores and the release of plasticizer as key degradation processes. Despite minimal structural modifications in PVAC, the loss of plasticizer leads to an increase in glass transition temperature, affecting the adhesive's cohesive strength and contributing to detachment of materials in artworks. The findings underscore the importance of preventive conservation measures to mitigate degradation issues in PVAC-based artworks.

A new di-mannitol adipate ester-based zinc metal alkoxide (DMAE-Zn) was synthesized as a bi-functional PVC thermal stabilizer for the first time. The materials were characterized with Fourier-transform Infrared spectroscopy (FT-IR) and thermogravimetric analysis (TGA). Characterization results confirmed the formation of Zn-O bonds in DMAE-Zn; and that DMAE-Zn had a high decomposition temperature and a low melting point. The thermal stability of DMAE-Zn on PVC also was tested by conductivity test, thermal aging test, and UV-visible spectroscopy (UV-VIS) test. PVC stabilized by DMAE-Zn had a good initial color and excellent long-term stability. UV-VIS also showed that the conjugated structure in PVC stabilized by DMAE-Zn was almost all of the triene, suggesting that the addition of DMAE-Zn would suppress the formation of conjugated structures above tetraene. Dynamic processing performance of PVC samples tested by torque rheometer indicated that, having a good compatibility with PVC chains in the amorphous regions, DMAE-Zn contributed good plasticizing effect to PVC. DMAE-Zn thus effectively demonstrates bi-functional roles, e.g., thermal stabilizers and plasticizers to PVC. Furthermore, FT-IR, HCl absorption capacity test, and complex ZnCl₂ test were also used to verify the thermal stability mechanism of DMAE-Zn for PVC.

After a survey on polymer plasticization theories and conventional criteria to evaluate polymer-plasticizer compatibility through the solubility parameter, an attempt to create a polymer-plasticizers polarity scale through solvatochromic dyes has been made. Since the Reichardt’s ET(30) dye is insoluble in rubber hydrocarbon polymers like polyisoprene, polybutadiene and styrene-butadiene copolymers and is not also useful for the evaluation of the hydrocarbons and ester plasticizers, the Nile Red solvatochromic dye was instead used extensively and successfully for this class of compounds. A total of 53 different compounds were evaluated with the Nile Red dye and wherever possible also with the ET(33) Reichardt’s dye. A very good correlation was then found between the Nile Red scale E(NR) and the Reichardt’s ET(30) scale for this class of compounds focusing on diene rubbers and their typical hydrocarbons and new esters plasticizers. Furthermore, the E(NR) scale shows also a reasonable correlation with the total solubility parameter calculated according to the Van Krevelen method. Based on the above results, some conclusion was made about the compatibility between the diene rubbers and the conventional plasticizers as well as some new and green plasticizer proposed for the rubber compounds.