The precipitate phases often play an important influence on the corrosion resistance of 2205 Duplex stainless steel (DSS). In the presented paper, the microstructure and corrosion resistance in the hot-rolled and cold-rolled 2205 DSS aging for different time at 850 °C was investigated by XRD, SEM and potentiodynamic polarization. It has been found that the Chi(χ) phase and Sigm(σ) phase were precipitated in turn after aging treatment of hot-rolled and cold-rolled materials, but the precipitate amount in cold-rolled material is much more than that of hot-rolled samples. The corrosion resistance of the solution-annealed cold-rolled material is similar to the hot-rolled material, but the corrosion resistance of cold-rolled material with precipitate is weaker than that of hot-rolled material after aging treatment. Pitting initiates preferentially in the Cr-depleted region from σ phase in aged hot-rolled 2205, and severe selective corrosion occurs on sigma/ferrite interfaces aged for a long aged lime. However, the initiation of pitting corrosion may take place at the phase boundary, defect and martensite in the aged cold-rolled 2205. The σ phase is further selectively dissolved by electrochemical method to investigate the difference of microstructure and corrosion behavior in hot-rolled and cold-rolled 2205 duplex stainless steel.

Cu,N-TiO₂ nanotube (Cu,N-TNT) is prepared through a novel magnetron sputtering and anodic oxidation method. Then the morphology, structure and physicochemical property of Cu,N-TNT was analyzed by XRD, SEM, TEM, EDX and UV-vis-DR. The results indicate that the evenly doped copper is beneficial to the transformation of the TNT from anatase to rutile and play a key role in the morphology of the Cu,N-TNT. The doped Cu and N in the TNT influence the growth orientation of the TiO₂ crystals, which result in the lattice distortion and wider the interplanar spacing 60s-Cu,N-TNT has less band gap and stronger absorption intensity in visible region than other Cu,N-TNT samples, which make the combination rate of photogenerated electron and photogenerated hole decrease greatly, thus beneficial to its physicochemical property.