Nanocomposites of cyanate ester resin (CER) filled with three different reactive amino-functionalized polyhedral oligomeric silsesquioxane (POSS) were synthesized and characterized. The addition of a small quantity (0.1 wt.%) of amino-POSS chemically grafted to the CER network led to increasing thermal stability of CER matrix. A significant increase of the glass transition temperature, Tg (DSC data), and the temperature of α relaxation, Tα (DMTA data), by 45-55 оС of CER matrix with loading of nanofillers was evidenced. CER/POSS films exhibited a higher storage modulus than that of neat CER in the temperature range investigated. It was evidenced that CER/aminopropylisobutyl (APIB)-POSS, CER/N-phenylaminopropyl (NPAP)-POSS, and CER/aminoethyl aminopropylisobutyl (AEAPIB)-POSS nanocomposites induced a more homogenous α relaxation phenomenon with higher Tα values and an enhanced nanocomposite elastic behavior. Furthermore, CER/amino-POSS nanocomposites possessed higher specific surface area, gas permeability (CO2, He), and diffusion coefficients (CO2) values than those for neat CER, due to increasing free volume of the nanocomposites studied that is very important for their gas transport properties. Permeability grew respectively by about 2 (He) and 3.5-4 times (СО2), and diffusion coefficient of CO2 increased approximately twice for CER/amino-POSS nanocomposites in comparison with the neat CER network. The efficiency of amino-functionalized POSS in improving the thermal and transport properties of the CER/amino-POSS nanocomposites increased in a raw of reactive POSS containing one primary (APIB-POSS) < eight secondary (NPAP-POSS) < one secondary and one primary (AEAPIB-POSS) amino groups. APIB-POSS had the least strongly pronounced effect, since it could form covalent bonds with the CER network only by reaction of one –NH2 group, while AEAPIB-POSS displayed the most highly marked effect, since it could easily be incorporated into the CER network via reaction of –NH2 and –NH– groups with –O–C≡N groups from CER.

Polyhedral oligomeric silsesquioxane (POSS) is a suitable nanoscale reinforcement for thermosetting polymers, such as epoxy resin systems in order to modify its mechanical, thermal, and chemical properties. The inclusion of POSS in the epoxy resin at higher loading (greater than 1 wt.%), however, introduces the ductility during the fracture behavior of these nanocomposites. Consequently, the J-integral is used to quantify the fracture behavior of these materials and characterize the crack growth resistance curve against stable crack growth. A range of nanocomposites is prepared by adding 0.5, 1, 3, 5, and 8 wt.% of glycidyl POSS into DGEBF epoxy resin cured with an amine-based curing agent. From the fracture toughness experiment the load-displacement result confirms that when the POSS reinforcement is greater than 1 wt.%, the fracture behavior of the nanocomposite changes from brittle to ductile. For both brittle and ductile nanocomposites, the addition of POSS molecules improves the crack initiation toughness. The development of POSS–POSS compliant domains are reported previously, is attributed for this change in the failure behavior. The fractured images of POSS–epoxy nanocomposites, obtained using scanning electron microscopy, show that the increase in fracture resistance at higher values of POSS loading occurs due to the extensive shear yielding. Meanwhile, the increased fracture toughness at lower values of POSS loading occurs due to crack pinning and crack deflection.