In this study, 3D printing of poly-l-lactic acid (PLLA) scaffolds reinforced with graphene oxide (GO) nanoparticles via Digital Light Processing (DLP) was investigated to mimic bone tissue. Stereolithography is one of the most accurate additive manufacturing method, but the dominant available materials used in this method are toxic. In this research, a biocompatible resin (PLLA) was synthetized and functionalized to serve the purpose. Due to the low mechanical properties of the printed product with the neat resin, graphene oxide nanoparticles in three levels (0.5, 1, and 1.5 Wt.%) were added with the aim of enhancing the mechanical properties. At first, the optimum post cure time of the neat resin was investigated. Consequently, all the parts were post-cured for three hours after printing. Due to the temperature-dependent structure of GO, all samples were placed in an oven at 85 ° C for different time periods of 0, 6, 12, and 18 hours to increase mechanical properties. The compression test of heat treated samples reveals that the compressive strength of the printed parts containing 0.5,1, and 1.5 % of GO increased by 151,162 ad 235%, respectively. Scaffolds with the designed pore sizes of 750 microns and a porosity of 40% were printed. Surface hydrophilicity test was performed for all samples showing that the hydrophilicity of the samples increased with increasing GO percentage. The degradation behavior of the samples was evaluated in a PBS environment, and it revealed that by increasing GO, the rate of component degradation increased, but the heat treatment had the opposite effect and decreased the degradation rate. Finally, besides improving biological properties, a significant increase in mechanical properties under compression can introduce the printed scaffolds as a suitable option for bone implants.

Water pollution in developing countries affects the public health of humans and the environment. It is therefore essential to develop environmentally friendly biopolymer, sustainable and low-cost membranes. Biopolymer nanofiber membranes are made by an electrospinning process of polylactic acid (PLLA) with additives. The main objective of this study is to manufacture biodegradable nanofiber membranes for use in filtering the suspended elements in wastewater at the level of drinkable or in agricultural fields. It is known that PLLA is brittle and therefore it is difficult to apply in industry. To solve this problem and enhance its flexibility. Flexible biopolymer polypropylene carbonate (PPC) and plasticizer are the addition in PLLA to reduce its glass transition and enhance its crystallization by adding Poly(3-hydroxy butyrate) PHB. In this work, 20 wt% of PPC was added to PLLA matrix to improve its elasticity and elongation at break. DSC shows that the addition of PPC, PHB, and TEC did affect the thermal properties like T_g, T_cc and T_m of the PLLA blends. The position of the T_g, T_cc, and T_m is shifting, the consequence the chain mobility is increased, therefore the crystallinity is enhanced. Electrospun fibers of PLLA/PPC/PHB/TEC were successfully manufactured. Tensile tester showed the increase in elongation at break of PLLA blend films, the elongation at break increases by 285 times. It observed with the increasing the elongation at break, a decrease in stress strength. After improving the mechanical properties with the higher elongation at break values, this blend is optimal for filtrations process.

: This article reports on polymer (PLLA, poly(L-lactic acid)) nanosheets incorporated with Fe-ion nanoparticles, aiming at using the latter nanoparticles as source to release Fe ions to facilitate burn wound healing when such nanosheets are applied on skin as biomedical tissue. Laser ablation in liquid phase was used to produce Fe-containing nanoparticles that after incorporation into PLLA nanosheets would release Fe ions when in immersed in water. Such nanoparticles prepared in chloroform are shown by XPS to be based on iron chloride and oxide phases. After incorporation into PLLA nanosheets, the ion –release test demonstrated that Fe ions could be released successfully into water at pH 7.4, which implies that such polymer nanosheets show promise for biomedical applications as potential patches for healing burn wounds. Incorporation with two different metal ions (Fe and Zn) is shown to be efficient and both types of ions were demonstrated to be released simultaneously and with comparable release rates.

Optical rotatory dispersion (ORD) is a beautiful analytical technique for the study of chiral molecules and polymers. In this study, ORD was applied successfully to follow the degree of polycondensation of l-(+)-lactic acid toward the formation of poly(lactic acid) oligomers (PLAO) and high molecular weight poly(l-lactic acid) (PLLA) in a simple esterification reaction equipment. PLLA is a biodegradable polymer obtainable from renewable raw materials. The racemization of the intrinsically isotactic PLLA through thermal treatment can be easily followed through the use of ORD spectroscopy. Organic or molecular electronics is a hot topic dealing with the combination of π-conjugated organic compounds and polymers with specific properties (e.g. chirality) which can be exploited to construct optoelectronic devices such as organic light-emitting diodes (OLEDs), organic photovoltaic (OPV) high efficiency cells, switchable chirality devices, organic field-effect transistors (OFETs), and so on. ORD spectroscopy was applied to study either the gigantic optical rotation of PLLA films as well as to detect successfully the excitonic coupling occurring in thin solid PLLA green film loaded with a combination of two dyes: SY96 (a pyrazolone dye) and PB16 (the metal-free phthalocyanine pigment). The latter compound PLLA loaded with SY96 and PB16 shows a really gigantic optical activity in addition to typical ORD signal due to exciton coupling and may be considered as a simple and easily accessible model composite of a chiral polymer matrix combined with π-conjugated dyes for molecular electronics studies.

Here, we report on ZnO nanoparticles (NPs) generated by nanosecond pulsed laser (Nd:YAG, 1064 nm) through ablation of metallic Zn target in water and air and their comparative analysis as potential nanomaterials for biomedical applications. The prepared nanomaterials were carefully characterized in terms of their structure, composition, morphology and defects. It was found that in addition to the main wurtzite ZnO phase, which is conventionally prepared and reported by others, the sample laser-generated in air also contained some amount of monoclinic zinc hydroxynitrate. Both nanomaterials were then used to modify model wound dressings based on biodegradable poly-L-lactic acid. The as-prepared model dressings were tested as biomedical materials with bactericidal properties towards S. aureus and E. coli strains. The advantages of the NPs prepared in air over their counterparts generated in water found in this work are discussed.