Synthesis of biocompatible and bioresorbable composite materials such as “polymer matrix-mineral constituent,” which stimulate the natural growth of living tissues and the restoration of damaged parts of the body, is one of the challenging problems in regenerative medicine and material science. Composite films of bioresorbable polymer of polyvinylpyrrolidone (PVP) and hydroxyapatite (HA) were obtained. HA was synthesized in situ in a solution of polymer mixture. We applied electron paramagnetic resonance (EPR) and nuclear magnetic resonance (NMR) approaches to study their properties. EPR in two frequency ranges allowed to derive spectroscopic parameters of the nitrogen-based light and radiation-induced paramagnetic centers in HA, PVP and PVP-HA with high accuracy. It was shown that PVP did not significantly affect the EPR spectral and relaxation parameters of the radiation-induced centers in HA. Magic angle spinning (MAS) 1H NMR shows the presence of two signals at 4.7 ppm and -2.15 ppm attributed to “free” water and hydroxyl groups, while the single line - to 31P. NMR relaxation measurements for 1H and 31P show that the relaxation decays are a multicomponent process that can be described by three components of the transverse relaxation times. The obtained results demonstrated that the applied magnetic resonance methods can be used for the control of quality of the synthesis of the PVP-HA composites and, potentially, for the development of analytical tools to follow the processes of the sample treatment, resorption, and degradation.

Ceramic samples based on b-calcium pyrophosphate b-Ca2P2O7 were prepared using firing at 900, 1000, and 1100 oC from powders of g-calcium pyrophosphate g-Ca2P2O7 with preset molar ratios Ca/P=1; 0,975 and 0,95. To prepare powders of g-calcium pyrophosphate g-Ca2P2O7 with preset molar ratio Ca/P=1; 0,975 and 0,95 powder mixtures based on calcium lactate pentahydrate Ca(C3H5O3)2⋅5H2O and, monocalcium phosphate monohydrate Ca(H2PO4)2⋅H2O were treated in an aqua medium in mechanical activation conditions, dried, disaggregated in acetone, and heat-treated at 600 oC. The phase composition of powder mixtures after treatment if planetary mill in aqua medium included both brushite CaHPO4⋅2H2O or monetite CaHPO4, and starting salts. The phase composition of all powder mixtures after disaggregation in acetone in planetary mill included monetite CaHPO4 and starting salts. After heat treatment at 600 oC according to the XRD data phase composition of all powder mixtures was presented by g-calcium pyrophosphate g-Ca2P2O7. The grain size of ceramics increased both with the growth of firing temperature and with decreasing of molar ratio Ca/P of powder mixtures. Calcium polyphosphate (t melt =960–968 oC) formed from monocalcium phosphate monohydrate Ca(H2PO4)2⋅H2O acted like a liquid phase sintering additive. It was confirmed by tests in vitro, that prepared ceramic materials with preset molar ratio Ca/P=1; 0,975 and 0,95 and phase composition presented by b-calcium pyrophosphate b-Ca2P2O7 according to XRD data were biocompatible and could maintain bone cells proliferation.

The development of magnesium calcium phosphate bone cements (MCPCs) have garnered big attention. MCPCs are bioactive and biodegradable and have appropriate mechanical and antimicrobial properties for use in reconstructive surgery. In this study, the cement powders based on a (Ca + Mg)/P = 2 system doped with Zn2+ at 0.5 and 1.0 wt.% were obtained and investigated. After the mixing with a cement liquid, structural and phase composition, morphology, chemical structure, setting time, compressive strength, degradation behavior, solubility, antibacterial activities, and in vitro behaviour of the cement materials were examined. A high compressive strength of 48 ± 5 MPa (mean ± SD) was achieved for the cement made from Zn2+ 1.0-wt.%-substituted powders. The Zn2+ introduction led to antibacterial activity against Staphylococcus aureus and Escherichia coli strains, with an inhibition zone diameter up to 8 mm. Biological assays confirmed that the developed cements are cytocompatible and promising as a potential bone substitute in reconstructive surgery.