Electrode degradation in continuous resistance spot welding process of BH 220 steel was evaluated by electrode life test, and weldability tests were conducted by geometry features measurement, mechanical property analysis, and electrode diameter measurement with 88 or 176 weld intervals. The analysis of weld geometry shows that the HAZ width, nugget diameter, and nugget area tend to decrease rapidly, while the nugget height tends to firstly increase with the weld repetitions till the welding heat input becomes too small to form the valid nugget. The peak load shows a rapid downward trend, while failure energy and maximum displacement slightly increase till the 176th weld and then decrease. The cavities and pores in the nugget mainly appear after the 176th spot weld. The electrode diameter increases during welding. The reason for the increase in electrode diameter may be that the contact area between the electrode and BH 220 steel sheets becomes smaller in the welding process, which causes the continuous sticking phenomenon between the electrode and the BH 220 steel sheets. In the absence of alloying, the edge of the electrode is geometrically deformed, while Cu-Zn-Fe alloying occurs in the area in contact with the BH 220 steel sheet.

The aim of this investigation is to offer a data-based scheme for predicting electrode wear in resistance spot welding. Electrode wear and alloying is one of the most significant factors that affect the mechanical properties of spot welds and the variation in weld quality. In this study, Rogowski coils and twisted pairs attached to the top and bottom electrodes were used to obtain the welding current and the inter-electrode voltage in the welding process, thereby calculating the dynamic resistance value during the welding process. The electrode diameter was obtained from the pressure exerted by the upper and lower electrodes on the carbon paper when the current was cut off and was regarded as an indicator of electrode wear. By continuously welding 0.5mm thick BH 340 steel plates until the electrode failed, the dynamic resistance signal was recorded in real time. Simultaneously, the electrode diameter after every 4 welds was also recorded. On this basis, the correlation between electrode diameter and dynamic resistance is studied. In order to quantitatively study the mapping relationship between dynamic resistance and electrode wear, 11 characteristic values were extracted from the dynamic resistance, and the stepwise regression method was used to obtain the regression formula between the characteristic values and the electrode diameter. Using new data to verify the effectiveness of the regression model, the acquired results display that the maximum error between the predicted value of the electrode diameter and the measured value obtained by the regression equation with the interactive quadratic term is 0.3 mm, and the corresponding relative error is 7.69 %. This result demonstrates that the method proposed in this paper can effectively monitor the electrode wear and failure process.