A series of Si-bearing MgAl₂O₄-spinels were synthesized at 1500-1650 °C and 3–6 GPa. These spinels had SiO₂ contents up to ~1.03 wt%, and showed a substitution mechanism of Si⁴⁺ + Mg²⁺ = 2Al³⁺. Unpolarized Raman spectra were collected from polished single grains, and displayed a set of well-defined Raman peaks at ~610, 823, 856 and 968 cm^-1 which had not been observed before. Aided with the Raman features of natural Si-free MgAl₂O₄-spinel, synthetic Si-free MgAl₂O₄-spinel, natural low quartz, synthetic coesite, synthetic stishovite and synthetic forsterite, we infer that these Raman peaks should belong to the SiO₄ groups. The relations between the Raman intensities and SiO₂ contents of the Si-bearing MgAl₂O₄-spinels suggest that at some P-T conditions some Si must adopt the M-site. Unlike the SiO₄ groups with very intense Raman signals, the SiO₆ groups are largely Raman-inactive. We have further found that the Si cations primarily appear on the T-site at P-T conditions ≤ ~3–4 GPa and 1500 °C, but attain a random distribution between the T-site and M-site at P-T conditions ≥ ~5–6 GPa and 1630–1650 °C. This Si-disordering process observed for the Si-bearing MgAl₂O₄-spinels hints that similar Si-disordering might happen to the (Mg,Fe)₂SiO₄-spinels (ringwoodite), the major phase in the lower part of the mantle transition zone of the Earth and the index mineral for the very strong shock stage experienced by extraterrestrial materials. The likely consequences have been explored.

Co-based catalysts have gained significant attention in recent years due to their excellent ability to activate C-H bonds and high selectivity towards olefins, despite being a non-noble and environmentally unfriendly metal. However, further improvements are necessary for practical utilization, particularly in terms of activity and anti-carbon deposition capacity. In this study, we synthesized Al₂O₃ nanorods with abundant pentacoordinated Al³⁺ (Al³⁺_penta) sites. The supported Co on the Al₂O₃ nanorod (Co/Al₂O₃-NR) exhibited higher selectivity (>96% propylene selectivity) and stability (deactivation rate 0.15 h^-1), compared to Co supported on an Al₂O₃ nanosheet with fewer pentacoordinated Al³⁺ sites. Various characterizations confirmed that Co(II) mainly exists as CoAl₂O₄ rather than Co₃O₄ in the form of Co/Al₂O₃-NR, which inhibits the reduction of Co(II) to Co0 and improves catalyst stability accordingly.

Reverse water gas shift reaction (RWGS) is an important process which plays a vital role in many CO2 utilization related reactions. Noble metals are the most active catalysts in RWGS, but the high price and low reserve strangled their applications. In the present work, we reported a non-transition-metal MgAl2O4 catalyst which showed outstanding activity and stability at high temperatures in the RWGS reaction and improved performance after doping of single atomic Nin+. The catalyst can obtain 46% of CO2 conversion in durability test of 75 h at 800 °C under high weight hourly space velocities (225 000 ml g-1 h-1). The adsorption sites, possible reaction route, and effects of Nin+ single atoms on the (111) surface of MgAl2O4 for RWGS were investigated by in situ DRIFTS and DFT calculations. The results indicated that the rate determining reaction step of RWGS on MgAl2O4 and Ni (SA)/MgAl2O4 were both the reaction of OH* + H* → H2O* + *, but the energy barrier was significantly reduced after introducing single atomic Nin+. Nin+ atoms can increase the hydroxyl coverage on the surface of catalyst and Al3+ sites near the Nin+ ion are considered as the predominant active sites for RWGS reactions.

In the present work report, the MgAl₂O₄and the Ag/MgAl₂O₄ samples were successfully synthesized by the modified hydrothermal and the isovolumetric impregnation methods, respectively. The structural properties of the prepared samples were systematically characterized by XRD, SEM, TEM, DRS, XPS and et al techniques. The photocatalytic degradation of methylene blue by the Ag/MgAl₂O₄ and MgAl₂O₄ samples was comparatively studied under UV lamp irradiation. The results revealed that the prepared Ag/MgAl₂O₄ (pH=6) samples were the most active among the samples in photocatalytic of methylene blue. Under UV lamp irradiation, the Ag/MgAl₂O₄ (pH=6) photodegradation of methylene blue reached to 89.6% within 120 min. And the Ag/MgAl₂O₄ (pH=6) complex photocatalysts displayed a high photochemical stability under repeated irradiation. Repeated irradiate the Ag/MgAl₂O₄ (pH=6) compound, which indicated it had a high photochemical stability.

Franklinite-Zincochromite-Gahnite solid solutions have been prepared by ceramic or coprecipitation method and its pigmenting capacity as cool ceramic pigments in different glazes (double and single firing frits and porcelain frit) was studied. XRD, UV-Vis-NIR diffuse reflectance, CIEL*a*b* colour analysis, bandgap measurement and the photocatalytic activity over the Orange II azoic dye were carried out for the characterization of samples. Following criteria of high red colouring capacity and high NIR reflectance at minimum Cr amount, Zn(Fe1.8Cr0.2), Zn(Al1.5Cr0.5) and Zn(Al1.3Cr0.5Fe0.2)O4 turn out to be the optimal compositions for an intense reddish cool pigment. All powders show a direct semiconductor behaviour with bandgap around 2 eV, falling in the visible range (620 nm), and according to literature, the associated photocatalytic activity over Orange II with visible light irradiation is moderate in all cases, but the Franklinite-Zincochromite Zn(Fe1.8Cr0.2) stands out.

MgAl oxide coatings containing MgO and MgAl2O4 phases were doped with CeO2 particles using plasma electrolytic oxidation (PEO) of AZ31 magnesium alloy in 5 g/L NaAlO2 water solution, with CeO2 particles added at concentrations up to 8 g/L. They underwent extensive inve-stigation into their morphology, chemical and phase compositions, and most importantly, photoluminescent (PL) properties and photocatalytic-activity (PA) in photodegradation of methyl orange (10 cm3 of 8 mg/L). The concentration of CeO2 particles in the aluminate electrolyte influences the amount of CeO2 particles incorporated into MgAl oxide coatings, but CeO2 particles have no signi-ficant effect on the surface morphology, thickness, or phase structure of the coatings. The PL emi- ssion spectrum of MgAl oxide coating is divided into two bands: one in the 350-600 nm range related to structural defects in MgO, and another much more intense in the 600-775 nm range attributed to F+ centres in MgAl2O4. Incorporated CeO2 particles do not have a significant effect on the PL intensity of the band in the red spectral region, but the PL intensity of the first band increases with the concentration of CeO2 particles. PA of MgAl/CeO2 oxide coatings is higher than that of pure MgAl oxide coatings. The highest PA was observed for MgAl/CeO2 oxide coatings formed in aluminate electrolytes with the addition of 2 g/L of CeO2 particles. The MgAl/CeO2 oxide coatings remained chemically and physically stable across multiple cycles, indicating their potential for applications.

The study experimentally investigated a novel approach for producing hydrogen from methane cracking in dielectric barrier discharge catalytic plasma reactor using a nanocatalyst. Plasma-catalytic methane (CH4) cracking was undertaken in a dielectric barrier discharge (DBD) catalytic plasma reactor using Ni/MgAl2O4. The Ni/MgAl2O4 was synthesised through co-precipitation followed customised hydrothermal method. The physicochemical properties of the catalyst were examined using X-ray diffraction (XRD), scanning electron microscopy - energy dispersive X-ray spectrometry (SEM-EDX) and thermogravimetric analysis (TGA). The Ni/MgAl2O4 shows a porous structure spinel MgAl2O4 and thermal stability. In the catalytic-plasma methane cracking, the Ni/MgAl2O4 shows 80% of the maximum conversion of CH4 with H2 selectivity 75%. Furthermore, the stability of the catalyst was encouraging 16 hours with CH4 conversion above 75%, and the selectivity of H2 was above 70%. This is attributed to the synergistic effect of the catalyst and plasma. The plasma-catalytic CH4 cracking is a promising technology for the simultaneous H2 and carbon nanotubes (CNTs) production for energy storage applications.

Sodium substitution Li1-xNaxMn2O4 cathodes were synthesized by a solid-state reaction method. The morphologies and crystal structures of Li1-xNaxMn2O4 were characterized by scanning electron microscopy (SEM) and X-ray diffraction (XRD), respectively. All Li1-xNaxMn2O4 samples exhibited a single phase LiMn2O4 spinel structure with good crystallinity. The effect of Na+ ions on the electrochemical performance of Li1-xNaxMn2O4 was investigated by galvanostatic charge-discharge test. The results showed that lithium substituted by sodium deteriorated its capacity retention but enhance its discharge capacity when it worked at large current densities. The initial discharge capacity was 114.2 mAh/g for Li0.94Na0.06Mn2O4, and 93.1 mAh/g remained after 300 cycles at a current density of 2220 mA/g in the voltage range 3.0–4.3 V at room temperature.

The surface configurations of the low-index facets of a set of spinel oxides are investigated using DFT+U calculations to derive surface energies and predict equilibrium nanoparticle shapes via the Wulff construction. Two very different conditions are investigated, corresponding to application either in heterogeneous catalysis or in electrocatalysis. First, the bare stoichiometric surfaces of NiFe₂O₄, CoFe₂O₄, NiCo₂O₄, ZnCo₂O₄ spinels are studied to model their use as high-temperature oxidation catalysts. Second, focusing attention on the electrochemical oxygen evolution reaction (OER), and on the CoFe₂O₄ inverse spinel as the most promising OER catalyst, we generate surface configurations by adsorbing OER intermediates, and, in an innovative study, we recalculate surface energies taking into account adsorption and environmental conditions, i.e., applied electrode potential and O₂ pressure. We predict that, under OER operating conditions, (111) facets are dominant in CoFe₂O₄ nanoparticle shapes, in fair agreement with microscopy measurements. Importantly, in the OER case we predict a strong dependence of nanoparticle shape upon O₂ pressure. Increasing O₂ pressure increases the size of the higher-index (111) and (110) facets at the expense of the (001) more catalytically active facet, whereas the opposite occurs at low O₂ pressure. These predictions should be experimentally verifiable and help define the optimal OER operative conditions.

The presence of high concentrations of flammable gases and volatile organic compounds in the atmosphere has been widely reported to be detrimental to human survival. A lot of research effort has been put towards finding an efficient means of quick detection of these gases below their ‘immediately dangerous to life or health’ concentrations. Detecting these gases in an oxygen-deficient environment is a crucial task to consider and has been overlooked. In this research, double substitution spinel with chemical formula Co1-2xNixMnxFe2-yCeyO4, where 0 ≤ x = y ≤ 0.3, were prepared via the glycol-thermal technique. The final products following the appropriate substitution are CoFe2O4 (dried naturally), CoFe2O4 (dried with Infrared lamp), Co0.8Ni0.1Mn0.1Fe1.9Ce0.1O4, Co0.6Ni0.2Mn0.2Fe1.8Ce0.2O4, and Co0.4Ni0.3Mn0.3Fe1.7Ce0.3O4 spinel ferrites. The X-ray diffractometry (XRD), High resolution transmission electron micrographs (HRTEM), and X-ray photoelectron spectroscopy (XPS) of the samples confirm the formation of the spinel. The gas sensing performance of this samples were tested at operating temperature of 225 ºC towards liquefied petroleum gas (LPG), ammonia, ethanol, and propanol. The Co0.8Ni0.1Mn0.1Fe1.9Ce0.1O4-based sensor was selective to LPG, with a high response of 116.43 toward 6 000 ppm of LPG when helium was used as carrier gas, 3.35 when dry-air was the carrier gas, 4.4 when nitrogen was the carrier gas, but was not sensitive when argon was used as a carrier gas.

This paper seeks to examine how the Mn-Co spinel interconnect coating microstructure can in-fluence the Cr contamination in an oxygen electrode of intermediate temperature Solid Oxide Cells at the operating temperature of 750 °C. A Mn-Co spinel coating is processed on Crofer 22 APU substrates by electrophoretic deposition and subsequently sintered following both the one-step and two-step sintering, in order to obtain significantly different densification levels. The electrochemical characterization is performed on anode supported cells with a LSCF cathode. The cells were aged prior to the electrochemical characterization in contact with the spinel coated Crofer 22 APU at 750 °C for 250 hours. Current-voltage and impedance spectra of the cells were measured after the exposure with the interconnect. Post-mortem analysis of the interconnect and the cell was carried out in order to assess the Cr retention capability of coatings with different microstructures.

The preparation of transition metal salt ammine complexes having oxidizing anions is a great challenge due to the reaction between the ammonia and oxidizing anions during the synthesis of these materials. However, they have an important role in the development of new oxidants in organic chemistry and especially as precursors in the preparation of mixed metal oxides and alloys in controlled temperature thermal decomposition reactions. Therefore, the synthetic procedures to prepare the complexes of transition metal permanganate, pertechnetate, and perrhenate (VIIB group tetraoxometallates) salts with ammonia as ligand or co-ligand have been comprehensively reviewed. The available data about the structure and spectroscopic properties of these compounds, including the hydrogen bonds that act as redox reaction centers under their thermal decomposition are given and evaluated. Their thermal decomposition processes and products have been summarized. The available pieces of information about their role in organic oxidation reactions like the oxidation of benzyl alcohols, and regeneration of oxo-compounds from oximes and phenylhydrazones including the kinetics of these processes have also been collected.

Vanadium containing slurry is a by-product of vanadium pentoxide by hydrometallurgical methods from vanadium slag. It is promising technogenic raw material for vanadium production. The phase analysis of vanadium-containing slurry by X-ray diffraction method has shown that it contains vanadium in spinel form (FeO∙V2O3). The various oxidation roasting methods for slurry treatment have been studied for increasing vanadium extraction into the solution. It has shown that the most effective additive is 1% CaCO3 at a roasting temperature of 1000 °C. The oxidation roasting of vanadium-containing slurry with the additive led to increase acid-soluble form of V2O5 from 1.5 to 3.7% and decrease the content of FeO∙V2O3 from 3 to 0.4%. These results have confirmed the efficiency of the application of oxidation roasting to convert vanadium compounds into acid-soluble forms. The conversion mechanism of spinel to acid-soluble phases during oxidation roasting with additives was investigated by thermogravimetric analysis and thermodynamic simulation. It has shown that the formation of acid-soluble calcium vanadates during oxidation roasting without additives occurs at temperatures above 800 °C, but СаСО3 addition allows to reduce this temperature to 600 °C.

Li-rich manganese-based cathode materials (LRMs) are considered one of the most promising cathode materials for the next generation lithium-ion batteries (LIBs) because of their high energy density. However, there are problems such as capacity decay, poor rate performance, and continuous voltage drop, which seriously limit their large-scale commercial applications. In this work, Li1.2Mn0.54Co0.13Ni0.13O2 coated with Li2MoO4 with unique spinel structure was prepared by wet chemistry method and the subsequent calcination process. The Li2MoO4 coating layer with spinel structure can provide a 3D Li+ transport channel, which is beneficial for improving rate performance, while protecting LRMs from electrolyte corrosion, suppressing interface side reactions, and improving cycling stability. The capacity retention rate of LRMs coated with 3wt% Li2MoO4 increased from 69.25% to 81.85% after 100 cycles at 1C, and the voltage attenuation decreased from 7.06 to 4.98 mV per cycle. The lower Rct also exhibits improved magnification performance. The results indicate that the Li2MoO4 coating effectively improves the cyclic stability and electrochemical performance of LRMs.