Low temperature dielectric property of charge/orbital ordered manganite, Pr1-xCaxMnO3 for 0.40≤x≤0.50 is investigated systematically as a function of Ca-content, x. The Ca-content dependence of dielectric permittivity and dissipation factor exhibit distinct maxima around x=0.45. The overall dielectric response of charge ordered Pr1-xCaxMnO3 is dominated by polarization induced by polaron hopping and exhibits thermally activated relaxation behaviour. The dielectric relaxation behaviour over the investigated temperature range is analysed with the help of small polaron hopping model and as well as variable range hopping model. The estimated polaron parameters also display non-monotonic variation with x and exhibit broad minima between x=0.425-0.45. The observed results suggest that a modulation of checker board type charge ordering pattern in Pr1-xCaxMnO3 is possibly taking place in the Ca-content range of investigation 0.40≤x≤0.50.

The effects of an external strain tensor on the electrical resistivity of a manganite granular system are investigated using a simple approach describing the induced deformation in terms of the tilt angle between adjacent grains. The results obtained assuming the resistivity of each grain as given by a metallic part, coming from the inner grain, and a surface related tunnel contribution, allow to estimate appreciable resistivity variations even in the case of small deformation angles.

This report aimed to know the performance of local mineral-based composite ceramic. The materials used consist of Indonesian local minerals, which are jarosite and manganite minerals as sources of oxide iron and Mangan. The materials were synthesized using the precipitation method, whereas composite ceramic was fabricated using a screen printing method and fired at 600 oC using a furnace. The results of the characterizations indicate that the sample forms three phases on diffraction peaks. The differences in the resistance values in ambient and ethanol environments indicate that the sample has very different responses. The high porosity of the sample greatly support the gas adsorption process. Thus, the sample has a high level of sensitivity. With the above characteristics, the composite ceramic which was fabricated has the potential to be applied to gas sensors, especially ethanol gas sensors.

This work shows a correlation between light reflectance, absorption, and morphologies of series of (1-x) BM–x PT, (x = 0.0, 0.02, 0.04, 0.08, 0.12, 0.16, 0.24) ceramics composite. The (1-x) BM–x PT showed features of a black mirror with a low optical energy gap. The measured Vis-NIR diffused reflectance enabled the calculation of the energy gap using the modified Kubelka-Munk function. The estimated energy gap was lower than 1.5 eV related to low reflectance in the Vis-NIR range. Moreover, obtained histograms of grains, using scanning electron microscope, enabled the correlation between grains size and amount of lead titanate. We deduced from the ceramics surface morphology that marked porosity also induced reflectivity of low magnitude. We correlated the magnitude of the energy gap with phases of the BM-PT composite and with the electrical conductivity activation energy reported in the literature. Our results findings opened prospect studied materials for optical applications.