Economic development and population growth lead to increased production of chicken manure (CM), which is a problematic organic waste for its amount, environmental threats, and moisture content. There are different ways of CM, namely anaerobic digestion, composting, combustion, and direct land spreading. Hydrothermal carbonization (HTC) is another emerging way, however. In this study, the HTC of CM was performed to produce energy-rich material called hydrochar (HC). The effects of HTC temperature (180, 240, 300 C) and process time (30, 90, 180 min) were summarized. Proximate and ultimate analysis, as well as heating values (HHV, LHV), have been performed both on raw CM and derived HC. Additionally, the process performance has been examined. The obtained results show that HTC is a feasible method for CM disposal and valorization. Although process time did not influence considerably fuel properties of CM, higher temperature led to significantly higher HHV, reaching 23,880.6734.56 Jg-1 at 300 C and 180 min with an improvement of 8,329 Jg-1 compared with raw CM (15,551.67 Jg-1). The process conducted at 240 C in 30 min has been specified as the most favorable, due to the highest energy gain of HC and relatively low energy consumption.

In this study, 12 organic waste materials were subjected to TG/DTG thermogravimetric analysis and DSC calorimetric analysis. These analyses provided basic information about thermochemical transformations and degradation rates during organic waste pyrolysis. Waste materials were chosen to cover the most abundant waste that can be found in the municipal solid waste stream. Based on TG results, kinetic parameters according to Coats–Redfern method were determined. The pyrolysis activation energy was the highest for cotton 134.5 kJ∙(mol∙K)-1 and the lowest for leather 25.2 kJ∙(mol∙K)-1. The DSC analysis showed number of transformations occurred during pyrolysis for each material. For each transformation, normalized energy required for transformation, or released during transformation were determined and then summarized to present energy balance. The study found that only for three waste materials: PET (-220.1 J⸱g-1), leather (-66.9 J⸱g-1), and chicken meat (-130.3 J⸱g-1) energy balance was negative, while the highest positive balance value was found for potato peelings (367.8 J⸱g-1). The obtained results may be applied for the modelling of energy and mass balance of municipal solid waste pyrolysis.