This work discussed the advantages of reducing copper in molten copper slag with low S content. FactSage calculated the distribution of copper at equilibrium under different sulfur content. The effect of sulfur content on copper recovery under different oxygen partial pressures was pointed out. The effect of sulfur content on copper recovery in the actual reduction process was explored through experimental research. Under the condition of low sulfur, the Recovery of copper and the stability of the experiment have an ideal results.

Tungsten carbide (WC) was well known as a wear-resistant material. Iron-based pow-der was suitable for remanufacturing of cast iron engine parts. To improve the wear resistance of the remanufactured iron-based cast iron engine parts, WC-Co was intro-duced into iron-based powders to prepare composite coatings for cast iron engine components. In this work, FeAlC-x(WC-Co) composite coatings were prepared by plasma transfer arc on compacted graphite cast iron. The influences of WC-Co con-tents in the Fe-AlC-x(WC-Co) composite coatings on the microstructure and properties of the composite coatings were investigated. The composite coatings contained γ-Fe, α-Fe, WC and Fe3W3C mainly. The microhardness of FeAlC-x(WC-Co) composite coatings had the highest hardness of 814 HV0.2, the-lowest coefficient of 0.5 and the lest wear mass loss of 1.3mg when the weight content of WC-Co in the composite coating was 20wt%. As compared with the FeAlC coating, FeAlC-x(WC-Co) composite coating achieved the effect of reducing friction and wear resistance simultaneously, which resulted from the self-lubricating effect of graphite and high wear-resistance of carbides in the claddings.