The effects of post-treatment temperature-based methods on 1D single PLA filaments after FFF have been studied. This lets to decouple the variables related to the 3D structure (layer height, raster angle, infill density, and others) from the variables solely related to the material (molecular weight, molecular orientation, crystallinity, and others). PLA 1D filaments have been aged at 20, 39, 42, 51, 65, 75 and 80 ºC in a water-bath-inspired process in which the hydrolytic degradation of the PLA has been minimised for the ageing temperatures of interest. The evolution of the thermal and mechanical properties of the PLA filaments at different temperatures was recorded. Differential scanning calorimetry (DSC) was used to evaluate thermal and physical properties, in which the glass transition, enthalpic relaxation, crystallisation and melting reactions were analysed. Tensile tests were performed to evaluate the tensile strength and elastic modulus. The flow-induced molecular orientation, the degradation, the logistic fitting and the so-called summer effect –stabilisation of properties at higher temperatures– are discussed for assessing the safeness of accelerating ageing.

The effect of Mg particles on PLA's thermal, chemical, physical, and mechanical properties has been studied. The thermal and physical properties have been studied by differential scanning calorimetry, analysing the stability of the α and α’-crystals of the PLA. A colloidal route was used to introduce Mg particles inside the PLA matrix, ensuring a good dispersion of the particles. Materials with Mg contents from 0 to 10 wt.% have been prepared, with additions of polyethyleneimine (PEI) and polyethylene glycol (PEG). Fourier Transform Infrared Spectroscopy has been used to confirm the influence of Mg, PEI, and PEG on PLA properties. The mechanical properties have been measured with a universal tensile test machine on printed filaments via Fused Filament Fabrication (FFF), which were naturally aged to stable conditions. Filaments with and without a notch were studied to obtain the materials' tensile strength, elastic modulus, and fracture toughness. Different analytical models to explain the results of the PLA-Mg were studied, in which the interface strength of the PLA-Mg composites was calculated.