Polymer flooding is an established enhanced oil recovery (EOR) method, still many aspects of polymer flooding are not well understood. This study investigates the influence of mechanical degradation on flow properties of polymers in porous media. Mechanical degradation due to high shear forces may occur in the injection well and at the entrance to the porous media. The polymers that give high viscosity yields at a sustainable economic cost are typically large, MW > 10 MDa, and have wide molecular weight distributions. Both MW and the distributions are altered by mechanical degradation, leading to changes in the flow rheology of the polymer. The polymer solutions were subjected to different degrees of pre-shearing and pre-filtering before injected into Bentheimer outcrop sandstone cores. Rheology studies of injected and produced polymer solutions were performed and interpreted together with in-situ rheology data. The core floods showed a predominant shear thickening behavior at high flow velocities which is due to successive contraction/expansion flow in pores. When pre-sheared, shear thickening was reduced but with no significant reduction in in-situ viscosity at lower flow rates. This may be explained by reduction in the extensional viscosity. Furthermore, the results show that successive degradation occurred which suggests that the assumption of the highest point of shear which determines mechanical degradation in a porous media does not hold for all field relevant conditions.

This paper presents an investigation into the influence of drag-reducing polymer (DRP) on the flow of water inside and around U-bends. The DRPs tested were partially hydrolysed polyacrylamide (HPAM) and two different molecular weight polyethylene oxides (PEO). The Reynolds number and in-situ concentration ranges of water and DRP were and respectively. The test section was made up of clear polyvinyl chloride (CPVC) pipes that contained two U-bends with radii of curvature (R) of 100 and 200 mm as well as straight sections of 19-mm ID. Higher pressure gradient was recorded in the under-developed flow section after the bend. Drag reduction (DR) increased with in-situ concentration of the DRP and the flowrate up to some threshold values. The concentration and flowrate thresholds were about 20 ppm and 1.07 m/s respectively. DR differed among the different sections considered with the highest values recorded for developed flows upstream of the bend and the least values recorded in the bend. DR at station 1 (immediately after the bend) was generally lower than that at station 2 (further downstream). P-K Plots showed that, the DR envelop for developed flow in straight pipes did not apply to the bend and the under-developed flow section. DR increased with polymer molecular weight and ionic strength in straight sections. However, molecular weight (and polymer shearing) had limited effect on DR in the bends. DR characteristics at the bend suggested that there was a different or additional mechanism. The effect of bend curvature ratio on DR was predominant after the U-bend. The larger the ratio of pipe diameter to bend diameter, the lower the DR in the redeveloping sections after the bend. For R = 100 mm, the highest DR recorded for fully developed flows before bend, in the bend, at stations 1 and 2 were 57, 31, 36 and 33% respectively while that for R = 200 mm were 64, 28, 42 and 49% respectively.

Water soluble polymers have gained an increasing interest in enhanced oil recovery (EOR) processes, especially as polymer flooding. Despite the fact that the flow of polymer in porous medium has been a research subject for many decades with numerous publications, there are still some research areas that need progress. The prediction of polymer injectivity remains elusive. Polymers with similar shear viscosity might have different in-situ rheological behaviors and may be exposed to different extent of mechanical degradation. Hence, determining polymer in-situ rheological behavior is of great significance for defining its utility. In this study, an investigation of rheological properties and mechanical degradation of different HPAM (partially hydrolyzed polyacrylamide) polymers was performed using Bentheimer sandstone outcrop cores. Results show that, HPAM in-situ rheology is different from bulk rheology measured in rheometer. Specifically, shear thickening behavior occurs at high rates, and near-Newtonian behavior is measured at low rates in porous media. This deviates strongly from measurements in the rheometer. Polymer molecular weight and concentration influence its viscoelasticity and subsequently its flow characteristics in porous media. Exposure to mechanical degradation by flow at high rate through porous media leads to significant reduction in shear thickening and thereby improved injectivity. More importantly, the degraded polymer maintained in-situ viscosity at low flow rates indicating that improved injectivity can be achieved without compromising viscosity at reservoir flow rates. This is explained by reduction in viscoelasticity. Mechanical degradation also leads to reduced residual resistance factor (RRF), especially for high polymer concentrations. For some of the polymer injections, successive degradation (increased degradation with transport length in porous media) was observed. The results presented here may be used to optimize polymer injectivity.