Hierarchical micro-/mesoporous graphitic carbon spheres (HGCS) with a uniform diameter of ~0.35 μm were synthesized by Fe-catalyzed graphitization of amorphous carbon spheres resultant from hydrothermal carbonization. The HGCS resultant from 3 h at 900 °C with 1.0 wt% Fe catalyst had high graphitization degree and surface area as high as 564 m²/g. They also exhibited high specific capacitance of 140 F/g at 0.2 A/g, good electrochemical stability with 94% capacitance retention after consecutive 2500 cycles. The graphitization degree of the HGCS contributed about 60% of their specific capacitance, and their specific capacitance per unit surface area was as high as 0.2 F/m² which was much higher than in the most cases of porous amorphous carbon materials reported before. In addition, the HGCS showed a high adsorption capacity of 182.8 mg/g for methylene blue (MB), which was 12 times as high as that in the case of carbon spheres before graphitization.

Nickel is widely used in industrial processes and plays a crucial role in many applications. However, most of the nickel resource mainly exists as nickel oxide in laterite nickel ore with complex composition, resulting in difficulty in upgrading the nickel content using physical separation methods. In this study, high-grade ferronickel concentrates were obtained through a carbothermal reduction and magnetic separation using laterite nickel ore and anthracite as raw materials. The effects of different types of additives (CaF2, Na2SO4 and H3BO3), carbon ratio (nc/no in metal oxides) and grinding time on the recoveries and grades of ferronickel concentrates were experimentally investigated, along with the microstructure and chemical composition of the products. CaF2 was proved to be the primary active additive in the aggregation and growth of the ferronickel particles, and the improvement of the grade of the product. Under the optimal conditions of CaF2 addition of 12 wt.%, carbon ratio of 1.4, and grinding time of 240 s, high-grade magnetically separable ferronickel concentrate with nickel grade 8.93 wt.% and iron grade 63.96 wt.% was successfully prepared. This work presents a practical method for the highly efficient recovery and utilization of iron and nickel from low-grade laterite nickel ore, contributing to the development of strategies for the sustainable extraction and utilization of nickel resources.