The paper investigates experimentally the influence of the Fused Filament Fabrication (FFF) pre-processing strategy on the tribological properties of parts made of PEI (polyetherimide), investigating the difference in the weight loss of the samples caused by abrasive wear before and after the test. The samples were tested for abrasive wear resistance on a tribometer constructed according to ASTM G65/16 (dry sand). Two types of specimen printing orientation along X-axis (lengthwise) and along Z-axis (heightwise) were tested in the study. Three types of path generation strategies were used for manufacturing "X" and "Z" specimens and totally 18 samples were made and tested. Path deposition strategy was carried out with path deposition width of 0.5mm and parallel paths in all slicing layers. In order to reduce the voids in volume, deposition path axes in subsequent layers were shifted by 0.25mm offset. Garnet abrasive Fe3Al2(SiO4)3 was used for this test. The analysis of the experimental data shows the relationship between the samples building direction (X, Z), applied deposition strategies (1X - 3X and 1Z - 3Z) on the resulting resistance to abrasive wear.Keywords: PEI, FFF, path generation strategy, abrasive wear

Nowadays, when milling complex parts or curved surfaces, we encounter several problems that must be taken into account in the production process. There are various factors that affect the quality and accuracy of production. The main objective of this paper was to analyze the size of the effective tool diameter when machining a shaped surface with respect to the selected position, namely at the perpendicular position of the tool. At the same time, the distribution of the engagement area on the tool surface was evaluated by extracting the area content and volume data at the point of contact. The experiment was also intended to highlight the importance of the choice of finishing strategy in a CAM system. The results showed that the tool engagement size corresponded to the extracted data describing the area and volume size for each tool position with respect to the curvature of the surface. The negative deviations obtained by the scanning method were due to machining close to the tool centre, which was affected by the changing effective tool diameter.

Clinching is a manufacturing method of mechanical joining two or more materials without the use of heat or additional components. This process relies on high plastic deformation to create a secure bond. Clinching technology is widely used for joining various grades and thickness of materials. Especially in the automotive industry, clinching is an alternative to spot resistance welding. However, the load-bearing capacity of clinched joints is comparatively lower when compared to resistance spot welded joints. This research aimed to enhance the load-carrying capacity of clinched joints. Experimental tests were conducted on clinched joints with locally modified microstructures to optimize their placement within the joint. The microstructure distribution in the clinched joint region was analysed using light and scanning electron microscopy, as well as microhardness measurements. Two material grades, micro-alloyed steels HX420LAD+Z and dual-phase ferritic-martensitic steels HCT600X+Z, were tested. Each grade underwent five groups of ten samples, subject to identical experimental conditions of local heating by resistance spot welding (RSW) and clinching. The application of RSW to the clinched joint area resulted in increase of load-bearing capacity for both joined types of materials.