This study is follow-up of the steel shot transformation under the influence of environmental factors research (Lisin et al., 2022) and is the initial stage of investigating the iron behavior in soils during steel shot corrosion under a number of factors: the metallic lead in soils, atmospheric precipitation, excess organic matter. The results obtained show that corrosion of steel ammunition is a continuous process, including the formation of a poorly soluble rust crust on the surface of the steel and the mineralization of the metal until it is destroyed. As a result, the metal transformed into rust form, is a constant source of iron ions and dispersed rust particles migrating in soil waters and accumulating in soils. In addition, the aggregation of corrosion products of steel ammunition is the cause of a change in physical and mechanical properties of soils, which leads to a violation of the air and water migration regime of soils and an increase in surface runoff from the territories of shooting activity. The highest environmental risks are observed when steel ammunition is used on shooting areas where metallic lead intensifies steel shot corrosion rate, while the deposited steel shot activates the deterioration of previously encapsulated metal and — if steel and lead ammunition are used at the same time — slows down the encapsulation of newly deposited metallic lead, which catalyses the accumulation and migration of lead in environmental components.

This paper presents the results of an experimental study of the patterns of steel and lead shot transformation under the impact of environmental factors (two types of shot exposed alone and in combination with each other). The analyzed environmental factors include atmospheric precipitation of various acidity and soil solutions with a higher content of organic acids. This research demonstrated that steel shot is characterized by a high transformation rate that is an order of magnitude higher on average than the transformation rate of lead under the same conditions. The prevalence of the suspended iron form (excluding the interaction with organic acids) presents risks for such environmental components as soils and sediments and may be hazardous to the ambient air and natural waters in case of wind erosion and surface runoff from the catchment area. Furthermore, the joint presence of steel and lead shot mutually accelerates the corrosion of both metals, thus increasing the environmental risks.