Sr4Al6O12SO4 samples were obtained from the compound mixture formed by a solid–state reaction of Al2O3, SrSO4, and SrCO3. Samples were compacted at 100MPa to form pellets of 1 and 4cm in diameter and were sintered at 1400°C for 4 hours. The compound was analyzed by X–ray diffraction. Static immersion and wettability tests were performed to evaluate corrosion resistance in contact with Al–Si. Corrosion tests were carried out by immersion at 800, 900, and 1000°C for 24, 50, and 100 hours, while wettability was carried out at 900, 1000, and 1100°C for 2 hours. Subsequently, the samples were prepared metallographically. Samples were analyzed by optical microscopy, scanning electron microscopy, and image analysis. In general, reaction products consisting of alumina, spinel, oxides, and sulfates were found. The contact angles obtained were 124° to 135°. It is concluded that ceramic substrate Sr4Al6O12SO4 is resistant to corrosion by Al–Si alloy, since the slight thickness of the reaction products found in the samples (100μm) considering the severe conditions of the experiment: 1000°C and 100 hours of isothermal temperature. Furthermore, it can be said that Sr4Al6O12SO4 is not wettable by Al–Si alloys.

The aim of this work is the preparation of contact active antimicrobial films by blending copolymers with quaternary ammonium salts and polyacrylonitrile as matrix material. A series of copolymers based on acrylonitrile and methacrylic monomers with quaternizable groups were designed with the purpose of investigating the influence of their chemical and structural characteristics on the antimicrobial activity of these surfaces. The biocide activity of these systems was studied against different microorganisms, such as the Gram-positive bacteria Staphylococcus aureus and the Gram-negative bacteria Pseudomona aeruginosa and the yeast Candida parapsilosis. The results confirmed that parameters such as flexibility and polarity of the antimicrobial polymers immobilized on the surfaces strongly affect the efficiency against microorganisms. In contrast to the behavior of copolymers in water solutions, when they are tethered to the surface, the active cationic groups are less accessible and then the mobility of the side chain is critical for a good contact with the microorganism. Blend films composed of copolymers with high positive charge density and chain mobility present up to a more than 99.999% killing efficiency against the studied microorganisms.