Polyurethane (PU) foam adhesives were prepared from castor oil as a polyol with isocyanate poly (4,4′-methylene diphenyl isocyanate) (PMDI) using a solvent-free process. The NCO/OH molar ratio used for the preparation of PU foams was 1.5. Water, organosiloxane and dibutyltin dilaurate were blowing agent, surfactant and catalyst, respectively. Effects of the ratio of blowing agent and catalyst were adjusted to optimize the properties. The results show that 4 wt% of castor oil of catalyst and blowing agent minimizes water absorption and maximizes volume expansion in the PU foams. FT-IR analysis shows that urethane bond was formed by hydroxyl group of castor oil and –NCO group of isocyanate PMDI. More blowing agent and catalyst could improve the volume expansion ratio and reduce water retention of PU foams. It was found that Moso bamboo charcoal (Phyllostachys pubescens) or/and China fir wood particle (Cunninghamia lanceolate) composites with setting densities of 500 and 600 kg/m³ can be prepared from optimized castor oil-based PU foam adhesive at 100 °C for 5 min under a pressure of 1.5 MPa. Increasing the amount of bamboo charcoal decreases the equilibrium moisture content, water absorption and internal bonding strength of the composite. Notably, bamboo charcoal composite exhibits excellent dimensional stability. The optimized density and bamboo charcoal percentages of the composite were 500 kg/m³ and 50 to 100%. The castor oil-based PU composites containing bamboo charcoal fulfilled the CNS 2215 standards for particleboard. This dimensionally stable, low-density bamboo charcoal composite has high potential to replace current indoor building materials.

Rigid polyurethane foams were synthesized using a renewable polyol from the simple physical mixture of castor oil and crude glycerol. The effect of the catalyst and blowing agent in the foams properties was evaluated. The use of physical blowing agent (cyclopentane and n-pentane) allowed obtaining foams with smaller cells in comparison with the foams produced with a chemical blowing agent (water). The increase of water content caused a decrease of density, thermal conductivity, compressive strength and Young's modulus, which indicates that the increment of CO₂ production contributes to the formation of larger cells. Higher amount of catalyst in the foam formulations caused a slight density decrease and an increase small significance of thermal conductivity, compressive strength and Young's modulus values. These green foams presented properties that indicate a great potential to be used as thermal insulation, as density (23 - 41 kg m^-3), thermal conductivity (0.0128 – 0.0207 W m^-1 K^-1), compressive strength (45 - 188 kPa) and Young's modulus (3 - 28 kPa). These biofoams are also environmental friendly alternatives and can aggregate revenue to biodiesel industry, contributing for reduction of this fuel prices.

Our aim was to evaluate efficacy and safety of 30mL CaO alone or plus Asc in bowel preparation before colonoscopy. Two hundred and forty six patients were allocated randomly to ingest 2L PEG with 30mL CaO, 1L PEG with 30mL CaO plus 5g Asc, or 3L PEG. We used Boston Bowel Preparation Scale (BBPS) to evaluate bowel preparation efficacy. We also determined other outcomes such as procedure time, polyp or adenoma detection rate and adverse events (AEs). Of 282 patients recruited, 36 were excluded. Groups were matched for baseline characteristics except weight (P = 0.020) and body mass index (BMI) (P = 0.003). Patient’s satisfaction were higher in 2L PEG-CaO (P = 0.016) and 1L PEG-CaO-Asc groups (P = 0·017). Patients’ compliance was 67.5%, 71.4% and 80.5% in 3L PEG, 2L PEG-CaO and 1L PEG-CaO-Asc groups (P = 0.014). Adequate bowel preparation rate was 75%, 78.57% and 53.66% in 3L PEG, 2L PEG-CaO and 1L PEG-CaO-Asc groups (P = 0.021). There were no differences in terms of remaining outcomes. Despite an increase in patients’ satisfaction and compliance, 1L PEG-CaO-Asc significantly decreased adequate bowel preparation rate. However, 2L PEG-CaO improved the patients' satisfaction and compliance and increased adequate bowel preparation rate.

The castor plant (Ricinus communis L.) has been known since time immemorial in traditional medicine in the pharmacopeia of Mediterranean and eastern ancient cultures. Moreover, it is still used in folk medicine worldwide. Castor bean has been mainly recommended as anti-inflammatory, anthelmintic, anti-bacterial, laxative, abortifacient, for wounds, ulcers, and many other indications. Many cases of human intoxication occurred accidentally or voluntarily with the ingestion of castor seeds or derivatives. Ricinus toxicity depends on several molecules, among them the most important is ricin, a protein belonging to the family of ribosome-inactivating proteins. Ricin is the most studied of this category of proteins and it is also known to the general public, having been used for biocrimes in several cases. Here, the main steps of ricin research are reported with particular regards to its enzymatic activity, structure and cytotoxicity. Moreover, we discuss ricin toxicity for animals and humans, as well as the relation amongst bioterrorism and ricin and its impact on environmental toxicity. Ricin has also been of great utility to develop a number of immunotoxins specific for the elimination of unwanted cells, mainly cancer cells; some of these immunotoxins gave promising results also in clinical trials.