Glass samples (59.5 – x) B2O3 – 20Na2O – 20CaO – xV2O5 – Er2O3 – 0.5AgCl (x = 0 – 2.5 mol%) were prepared using melt – quenching method to investigate the structural and optical properties of the glass. The structural of the glass were characterized by using XRD, TEM and FTIR, meanwhile the optical properties were characterized by UV – VIS absorption. The XRD patterns confirmed the amorphous nature of the prepared glass samples. FTIR confirmed the presence of VO4, VO5, BO3, and BO4 vibration, and this result showed NBO increased with increasing vanadium concentration. The UV – Vis – NIR spectra exhibits six absorption band centered at 490, 520, 540, 660, 800, and 980 nm. The optical band gap (Eopt), Urbach energy and refractive index shown decrease, increase and increase, respectively. The Judd – Ofelt intensity parameter reveal the trends was Ω2 > Ω4 > Ω6. There are three emission bands at 516 nm, 580 nm, and 673 nm which are represented by 2H11/2 – 4I15/2, 4S3/2 – 4I15/2, and 4F15/2 – 4I15/2, respectively under 800 nm excitation was obtained.

We investigated fabrication of neodymium doped thin film optical waveguide-based devices as potential active sources for planar integrated optics. Liquid-phase epitaxial growth was used to fabricate neodymium-doped yttrium aluminum borate films on compatible lattice-matched un-doped yttrium aluminum borate substrates. We observed the refractive index contrast of the doped and un-doped crystal layers by differential interference contrast microscopy. In addition, characterization by X-ray powder diffraction, optical absorption and luminescence spectra demonstrated the crystal quality and uniformity and optical guiding of the resulting thin films.