Semi-destructive and non-destructive techniques are not commonly used for masonry as they are complex and difficult to perform. This paper describes validation of the following methods: semi-destructive and non-destructive, ultrasonic technique for autoclaved aerated concrete (AAC). The research subject was the compressive strength of AAC test elements with declared various density classes of: 400, 500, 600 and 700 (kg/m3) and various moisture levels. Empirical data including the shape and size of specimens, were established from tests on 494 cylindrical and cuboid specimens, and standard cube specimens 100×100×100 mm using the general relationship for standard concrete (Neville’s curve). The effect of moisture on AAC was taken into account while determining the strength fBw for 127 standard specimens tested at different levels of water content (w = 100%, 67%, 33% 23% and 10%). Defined empirical relations can be used to correct the compressive strength of dry specimens. For 91 specimens 100×100×100 mm, the P-wave velocity cp was tested with the transmission method using using the ultrasonic pulse velocity method with exponential transducers. The curve (fBw – cp) for determining the compressive strength of AAC elements with any moisture level (fBw) was established.

The area of Central and Eastern Europe, and thus Poland, is not exposed to effects of seismic actions. Any possible tremors can be caused by coal or copper mining. Wind, rheological effects, the impact of other objects or a non-uniform substrate are the predominant types of loading included in calculations for stiffening walls. The majority of buildings in Poland, as in most other European countries, are low, medium-high brick buildings. Some traditional materials, like solid brick (>10% of construction materials market) are still used. But autoclaved aerated concrete (AAC) and cement-sand calcium-silicate (Ca-Si) elements with thin joints are prevailing (>70% of the market) on the Polish market. Adding reinforcement only to bed joints in a wall is a satisfactory solution (in addition to confining) for seismic actions occurring in Poland that improves ULS and SLS. This paper presents results from our own tests on testing horizontal shear walls without reinforcement and with different types of reinforcement. This discussion includes 51 walls made of solid brick (CB) reinforced with steel bars and steel trusses, results from tests on 15 walls made of calcium-silicate (Ca-Si) and AAC masonry units reinforced with steel trusses and plastic meshes. Taking into account our own tests and those conducted by other authors, empirical relationships were determined on the basis of more than 90 walls. They are applicable to design and construction phase to determine the likely effect of reinforcement on cracking stress that damage shear deformation and wall stiffness.

The subject of the research are materials formed as a result of hydrothermal treatment, in this case cellular concretes, both traditional and modified with plastics (HIPS). There are two types of materials resulting from hydrothermal treatment: autoclaved sand-lime bricks and autoclaved concrete. Both in the case of ABK and silicates, the basic stubstrates used during their production are: lime, sand and water (cement is also added to cellular concrete). The article presents the methodology of testing the porous structure of autoclaved materials with the use of computed tomography. Aerated concrete (light autoclaved concrete) has a compressive strength of 2-6 MPa. The tests included aerated concrete modified with high-impact polystyrene, commonly known as HIPS. HIPS high-impact polystyrene is a thermoplastic polymer that is obtained by block-suspension polymerization of styrene with the addition of synthetic rubber. As a result of polymerization, small particles of polybutadiene remain in the polystyrene male, changing its physical and mechanical properties. The results from the content of air voids in the autoclaved concrete sample with HIPS were on average: 52.53%.