Alloys based on TiNi are widely used in various fields of technology and medicine. In the present work, we report on preparation of TiNi-alloy based wire with the shape memory effect, which was used for compression clips for surgery. Composition and structure of the wire, and its martensitic and physical-chemical properties were studied using SEM, TEM, optic microscopy, profilometry, mechanical tests, etc. The TiNi alloy was found to consist of B2 and B19' and secondary-phase particles of Ti2Ni, TiNi3 and Ti3Ni4. Its matrix was slightly enriched in Ni (50.3 at. % of Ni). Homogeneous grain structure was revealed (an average grain size of 19±0.3 μm) with equal quantities of grain boundaries of special and general types. Surface oxide layer provide improved biocompatibility and promote adhesion of protein molecules. Overall, the obtained TiNi wire was concluded to exhibit martensitic, physical and mechanical properties suitable for its use as an implant material. The wire was then used for manufacturing compression clips with the shape memory effect and applied in surgery. The medical experiment that involved 46 children demonstrated that the use of such clips in children with double-barreled enterostomies permitted to improve the results of surgical treatment.

TiNi alloys are very widely used materials for implant fabrication. When applied as rib replacement, they are required to be manufactured as combined porous-monolithic structure, ideally with a thin porous part well-adhered to its monolithic substrate. Additionally, good biocompatibility, high corrosion resistance and mechanical durability are also highly demanded. So far, all these parameters were not achieved in one material, which is why active search in the field is still underway. In the present work, we prepared new porous-monolithic TiNi materials by sintering a TiNi powder (0-100 µm) on monolithic TiNi plates followed by surface modification with high-current pulsed electron beam. The obtained materials were evaluated by a set of surface and phase analysis methods, after which their corrosion resistance and biocompatibility (hemolysis, cytotoxicity, and cell viability) were evaluated. Finally, cell growth tests were conducted. In comparison with flat TiNi monolith, the newly-developed materials were found to have better corrosion resistance, also demonstrating good biocompatibility and potential for cell growth on their surface. Thus, the newly-developed porous-on-monolith TiNi materials with different surface porosity and morphology show promise as potential new-generation implants for rib endoprostheses.